Zinc tellurium selenium based quantum dot

ABSTRACT

A core-shell quantum dot comprising zinc, a core comprising a first semiconductor nanocrystal material; and a semiconductor nanocrystal shell disposed on the core, wherein the core-shell quantum dot does not comprise cadmium, and does comprise zinc, tellurium, selenium, and aluminum.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation application of Application No. 16/851,509, filed Apr. 17, 2020, which claims priority to and the benefit of Korean Patent Application No. 10-2019-0045759 filed in the Korean Intellectual Property Office on Apr. 18, 2019, and all the benefits accruing therefrom under 35 U.S.C. §119, the content of which in its entirety is herein incorporated by reference.

BACKGROUND 1. Field

A quantum dot and a device including the same are disclosed.

2. Description of the Related Art

Unlike bulk materials, physical characteristics (e.g., energy bandgaps and melting points) of nanoparticles may be controlled by changing the nanoparticle sizes. For example, a semiconductor nanocrystal particle (also known as a quantum dot) is a crystalline material having a size of several nanometers. The semiconductor nanocrystal particle has a relatively small size and a large surface area per unit volume and exhibits a quantum confinement effect, and thus may have different properties than bulk materials having the same composition. A quantum dot may absorb light from an excitation source to be excited, and may emit energy corresponding to an energy bandgap of the quantum dot.

SUMMARY

An embodiment provides a cadmium-free quantum dot capable of realizing, e.g., exhibiting, improved color purity.

An embodiment provides a method of manufacturing the aforementioned quantum dot.

An embodiment provides an electronic device including the quantum dot.

In an embodiment, a core-shell quantum dot includes a core including a first semiconductor nanocrystal; and a semiconductor nanocrystal shell disposed on the core, wherein the core-shell quantum dot does not include cadmium, and does include zinc, tellurium, selenium, and aluminum.

An ultraviolet-visible (UV-Vis) absorption spectrum of the quantum dot may include a first absorption peak and a valley adjacent to the first absorption peak, and (Abs_(first) - Abs_(valley))/ Abs_(first) ≥ about 0.01

wherein Abs_(first) is an absorption intensity at a wavelength of the first absorption peak and Abs_(valley) is an absorption intensity at a lowest point of the valley.

The core-shell quantum dot may have a quantum efficiency of greater than or equal to about 5%.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be greater than or equal to about 0.05:1.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be greater than or equal to about 0.7.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be greater than or equal to about 0.8:1.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be greater than or equal to about 1:1.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be greater than or equal to about 1.5:1.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be greater than or equal to about 2:1.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be less than or equal to about 4:1.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be less than or equal to about 3.5:1.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be less than or equal to about 3:1.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be less than or equal to about 2.7:1.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be less than or equal to about 2.5:1.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be less than or equal to about 2.2:1.

In the core-shell quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be or less than or equal to about 2.0:1.

The first semiconductor nanocrystal may include zinc, tellurium, and selenium.

The semiconductor nanocrystal shell may include zinc and at least one of selenium and sulfur.

The first semiconductor nanocrystal or the core-shell quantum dot may not include manganese, copper, or a combination thereof.

The first semiconductor nanocrystal may include ZnTe_(x)Se_(1-x), wherein x is greater than or equal to about 0.5 and less than or equal to about 0.95.

The semiconductor nanocrystal shell may include ZnSe, ZnS, ZnSeS, or a combination thereof.

The core-shell quantum dot may have a maximum photoluminescent peak in a wavelength range of greater than or equal to about 480 nanometers (nm).

The core-shell quantum dot may have a maximum photoluminescent peak in a wavelength range of greater than or equal to about 490 nm.

A full width at half maximum (FWHM) of the maximum photoluminescent peak of the core-shell quantum dot may be less or equal to than about 50 nm.

The core-shell quantum dot may have quantum efficiency of greater than or equal to about 10 %.

An amount of the aluminum may be greater than or equal to about 0.01 moles with respect to 1 mole of tellurium.

An amount of the aluminum may be greater than or equal to about 0.05 moles with respect to 1 mole of tellurium.

An amount of the aluminum may be greater than or equal to about 0.1 moles with respect to 1 mole of tellurium.

An amount of the aluminum may be greater than or equal to about 0.15 moles with respect to 1 mole of tellurium.

An amount of the aluminum may be greater than or equal to about 0.2 moles with respect to 1 mole of tellurium.

The core-shell quantum dot may have a Zinc Blende crystalline structure as determined by an XRD analysis.

The core-shell quantum dot may have a size of greater than or equal to about 2 nm.

The core-shell quantum dot may have a size of less than or equal to about 20 nm.

The core-shell quantum dot may include an organic ligand and the organic ligand may include RCOOH, RNH₂, R₂NH, R₃N, RSH, RH₂PO, R₂HPO, R₃PO, RH₂P, R₂HP, R₃P, ROH, RCOOR′, RHPO(OH), RPO(OH)₂, R₂POOH, a polymeric organic ligand, or a combination thereof, wherein R and R′ are the same or different and are each independently a substituted or unsubstituted C1 to C40 aliphatic hydrocarbon group, a substituted or unsubstituted C6 to C40 aromatic hydrocarbon group, or a combination thereof.

The organic ligand may not include a poly-functional compound having a thiol moiety and at least one of an amino group and a carboxylic acid group. The organic ligand may not include a glutathione compound.

The core-shell compound may be water-insoluble.

The core-shell quantum dot may further include lithium.

An amount of the lithium may be greater than or equal to about 0.01 moles with respect to 1 mole of tellurium.

An amount of the lithium may be greater than or equal to about 0.05 moles with respect to 1 mole of tellurium.

An amount of the lithium may be less than or equal to about 0.2 moles with respect to 1 mole of tellurium.

An amount of the lithium may be less than or equal to about 0.15 moles with respect to 1 mole of tellurium.

An amount of the lithium may be less than or equal to about 0.1 moles with respect to 1 mole of tellurium.

In an embodiment, a quantum dot includes zinc, tellurium, selenium, and aluminum, the quantum dot does not include cadmium, and in the quantum dot, an amount of the aluminum with respect to one mole of tellurium may be greater than or equal to about 0.01.

The quantum dot may include ZnTe_(x)Se_(1-x), wherein x is greater than or equal to about 0.5:1 and less than or equal to about 0.95:1.

In the quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be greater than or equal to about 0.8:1.

In the quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be greater than or equal to about 1:1 or greater than or equal to about 2:1.

In the quantum dot, a mole ratio of tellurium with respect to selenium (Te:Se) may be less than or equal to about 2.7:1, less than or equal to about 2.5:1, less than or equal to about 2.3:1. The quantum dot may not include manganese, copper, or a combination thereof.

The quantum dot (or the core-shell quantum dot, hereinafter, also referred to simply as “quantum dot”) may not include a Group III-V compound (e.g., an indium phosphide). In a photoluminescence spectroscopy analysis of the quantum dot, a full width at half maximum (FWHM) of a maximum photoluminescent peak may be less than or equal to about 50 nm. The FWHM may be less than or equal to about 45 nm. The FWHM may be less than or equal to about 40 nm. The FWHM may be less than or equal to about 35 nm. The quantum dot may have a quantum efficiency of greater than or equal to about 2%.

An ultraviolet-visible (UV-Vis) absorption spectrum of the quantum dot may include a first absorption peak and a valley adjacent to first absorption peak, and an absorption intensity at a wavelength of the first absorption peak may be greater than an intensity of a lowest point of the valley.

A valley depth (VD) defined by the following equation may be greater than or equal to about 0.01, greater than or equal to about 0.1, or greater than or equal to about 0.2:

(Abs_(first)- Abs_(valley))/ Abs_(first)= VD

wherein Abs_(first) is an absorption intensity at the first absorption peak wavelength and Abs_(valley) is an absorption intensity at the lowest point of the valley.

In the ultraviolet-visible (UV-Vis) absorption spectrum of the quantum dot, the first absorption peak and the lowest point of the valley may be present in a wavelength range of greater than or equal to about 410 nm.

In the ultraviolet-visible (UV-Vis) absorption spectrum of the quantum dot, the first absorption peak and the lowest point of the valley may be present in a wavelength range of less than or equal to about 520 nm, for example, less than or equal to about 500 nm.

In an embodiment, a quantum dot (e.g., polymer) composite includes a (e.g., polymer) matrix; and a plurality of quantum dots dispersed in the polymer matrix,

wherein the plurality of quantum dots includes the aforementioned (core-shell) quantum dot.

The polymer matrix may include a cross-linked polymer, a binder polymer including a carboxylic acid group, or a combination thereof.

The cross-linked polymer may include a polymerization product of a photopolymerizable monomer including a carbon-carbon double bond, a polymerization product of the photopolymerizable monomer and a multiple thiol compound having at least two thiol groups (e.g., at a terminal end of the multiple thiol compound), or a combination thereof.

The quantum dot (e.g., polymer) composite may further include a metal oxide fine particle (e.g., dispersed in the polymer matrix).

In an embodiment, a display device includes a light source and a light emitting element (e.g., a photoluminescent element), wherein the light emitting element includes the aforementioned quantum dot-polymer composite and the light source is configured to provide the light emitting element with incident light.

The incident light may have a photoluminescence peak wavelength of about 440 nm to about 460 nm.

The light emitting element may include a sheet of the quantum dot polymer composite.

The display device may further include a liquid crystal panel, and

the sheet of the quantum dot polymer composite may be disposed between the light source and the liquid crystal panel.

The light emitting element may include a stacked structure including a substrate and a light emitting layer (e.g., a photoluminescent layer) disposed on the substrate, wherein the light emitting layer includes a pattern of the quantum dot polymer composite.

The pattern may include a repeating section (e.g., at least one repeating section) configured to emit light at a predetermined wavelength.

The display device may be configured to have color reproducibility of greater than or equal to about 80% measured in accordance with a BT2020 standard.

A cadmium-free quantum dot capable of providing light with an enhanced efficiency and a reduced FWHM at a desired wavelength may be provided. The (core-shell) quantum dot of an embodiment may be applied to, e.g., used in, various display devices, biolabeling (biosensor, bioimaging), a photodetector, a solar cell, a hybrid composite, or the like.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other advantages and features of this disclosure will become more apparent by describing in further detail exemplary embodiments thereof with reference to the accompanying drawings, in which:

FIG. 1 is a graph of Absorption (arbitrary units (a.u.)) versus Wavelength (nm) illustrating a definition of a valley depth of a UV-Vis absorption spectrum of a quantum dot according to an embodiment.

FIG. 2 is an exploded view of a display device according to an embodiment.

FIG. 3A is a schematic cross-sectional view of a display device according to an embodiment.

FIG. 3B is a schematic cross-sectional view of a display device according to an embodiment.

FIG. 4 is a schematic cross-sectional view of a display device according to an embodiment.

FIG. 5 is a schematic cross-sectional view of a display device according to an embodiment.

FIG. 6 is a UV-Vis absorption spectrum of Absorption (a.u.) versus Wavelength (nm) and photoluminescent spectrum of Intensity (a.u.) versus Wavelength (nm) of a quantum dot synthesized in Example 1.

FIG. 7 is a UV-Vis absorption spectrum of Absorption (Abs.) (a.u.) versus Wavelength (nm) of a quantum dot synthesized in Comparative Example 1.

FIG. 8 is a UV-Vis absorption spectrum of Absorption (a.u.) versus Wavelength (nm) of a quantum dot synthesized in Example 4.

FIG. 9 is a UV-Vis absorption spectrum of Absorption (a.u.) versus Wavelength (nm) of a quantum dot synthesized in Example 5.

DETAILED DESCRIPTION

Advantages and characteristics of this disclosure, and a method for achieving the same, will become evident referring to the following example embodiments together with the drawings attached hereto. However, the embodiments should not be construed as being limited to the embodiments set forth herein. Unless otherwise defined, all terms used in the specification (including technical and scientific terms) may be used with meanings commonly understood by a person having ordinary knowledge in the art. The terms defined in a generally-used dictionary may not be interpreted ideally or exaggeratedly unless clearly defined. In addition, unless explicitly described to the contrary, the word “comprise” and variations such as “comprises” or “comprising”, will be understood to imply the inclusion of stated elements but not the exclusion of any other elements.

Further, the singular includes the plural unless mentioned otherwise.

In the drawings, the thickness of layers, films, panels, regions, etc., are exaggerated for clarity. Like reference numerals designate like elements throughout the specification.

It will be understood that when an element such as a layer, film, region, or substrate is referred to as being “on” another element, it can be directly on the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly on” another element, there are no intervening elements present.

It will be understood that, although the terms “first,” “second,” “third” etc. may be used herein to describe various elements, components, regions, layers and/or sections, these elements, components, regions, layers and/or sections should not be limited by these terms. These terms are only used to distinguish one element, component, region, layer, or section from another element, component, region, layer, or section. Thus, “a first element,” “component,” “region,” “layer” or “section” discussed below could be termed a second element, component, region, layer, or section without departing from the teachings herein.

The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting. As used herein, “a”, “an,” “the,” and “at least one” do not denote a limitation of quantity, and are intended to include both the singular and plural, unless the context clearly indicates otherwise. For example, “an element” has the same meaning as “at least one element,” unless the context clearly indicates otherwise. “At least one” is not to be construed as limiting “a” or “an.” “Or” means “and/or.” As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items. It will be further understood that the terms “comprises” and/or “comprising,” or “includes” and/or “including” when used in this specification, specify the presence of stated features, regions, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, regions, integers, steps, operations, elements, components, and/or groups thereof.

Furthermore, relative terms, such as “lower” or “bottom” and “upper” or “top,” may be used herein to describe one element’s relationship to another element as illustrated in the Figures. It will be understood that relative terms are intended to encompass different orientations of the device in addition to the orientation depicted in the Figures. For example, if the device in one of the figures is turned over, elements described as being on the “lower” side of other elements would then be oriented on “upper” sides of the other elements. The exemplary term “lower,” can therefore, encompasses both an orientation of “lower” and “upper,” depending on the particular orientation of the figure. Similarly, if the device in one of the figures is turned over, elements described as “below” or “beneath” other elements would then be oriented “above” the other elements. The exemplary terms “below” or “beneath” can, therefore, encompass both an orientation of above and below.

“About” as used herein is inclusive of the stated value and means within an acceptable range of deviation for the particular value as determined by one of ordinary skill in the art, considering the measurement in question and the error associated with measurement of the particular quantity (i.e., the limitations of the measurement system). For example, “about” can mean within one or more standard deviations, or within ± 10% or 5% of the stated value.

Exemplary embodiments are described herein with reference to cross section illustrations that are schematic illustrations of idealized embodiments. As such, variations from the shapes of the illustrations as a result, for example, of manufacturing techniques and/or tolerances, are to be expected. Thus, embodiments described herein should not be construed as limited to the particular shapes of regions as illustrated herein but are to include deviations in shapes that result, for example, from manufacturing. For example, a region illustrated or described as flat may, typically, have rough and/or nonlinear features. Moreover, sharp angles that are illustrated may be rounded. Thus, the regions illustrated in the figures are schematic in nature and their shapes are not intended to illustrate the precise shape of a region and are not intended to limit the scope of the present claims.

As used herein, when a definition is not otherwise provided, “substituted” may refer to replacement of hydrogen of a compound or a group by a substituent of a C1 to C30 alkyl group, a C2 to C30 alkenyl group, a C2 to C30 alkynyl group, a C6 to C30 aryl group, a C7 to C30 alkylaryl group, a C1 to C30 alkoxy group, a C1 to C30 heteroalkyl group, a C3 to C30 heteroalkylaryl group, a C3 to C30 cycloalkyl group, a C3 to C15 cycloalkenyl group, a C6 to C30 cycloalkynyl group, a C2 to C30 heterocycloalkyl group, a halogen (-F, -Cl, -Br, or -I), a hydroxy group (-OH), a nitro group (—NO₂), a cyano group (-CN), an amino group (-NRR′ wherein R and R′ are independently hydrogen or a C1 to C6 alkyl group), an azido group (-N₃), an amidino group (—C(═NH)NH₂), a hydrazino group (—NHNH₂), a hydrazono group (═N(NH₂)), an aldehyde group (—C(═O)H), a carbamoyl group (—C(O)NH₂), a thiol group (-SH), an ester group (—C(═O)OR, wherein R is a C1 to C6 alkyl group or a C6 to C12 aryl group), a carboxyl group (—COOH) or a salt thereof (—C(═O)OM, wherein M is an organic or inorganic cation), a sulfonic acid group (—SO₃H) or a salt thereof (—SO₃M, wherein M is an organic or inorganic cation), a phosphoric acid group (—PO₃H₂) or a salt thereof (—PO₃MH or —PO₃M₂, wherein M is an organic or inorganic cation), or a combination thereof.

As used herein, when a definition is not otherwise provided, a hydrocarbon group refers to a group including (e.g., consisting of) carbon and hydrogen (e.g., an alkyl, alkenyl, alkynyl, or aryl group). The hydrocarbon group may be a group having a valence of one or greater formed by removal of at least one hydrogen atom from alkane, alkene, alkyne, or arene. In the hydrocarbon group, at least one methylene may be replaced by an oxide moiety, a carbonyl moiety, an ester moiety, -NH-, or a combination thereof.

As used herein, when a definition is not otherwise provided, “alicyclic hydrocarbon group” may refer to a C3 to C30 cycloalkyl group, a C3 to C30 cycloalkenyl group, or a C3 to C30 cycloalkynyl group.

As used herein, when a definition is not otherwise provided, “aliphatic” refers to a saturated or unsaturated linear or branched hydrocarbon group. An aliphatic group may be an alkyl, alkenyl, or alkynyl group, for example.

As used herein, when a definition is not otherwise provided, “alkyl” may refers to a linear or branched saturated monovalent hydrocarbon group (methyl, ethyl, hexyl, etc.).

As used herein, when a definition is not otherwise provided, “alkenyl” refers to a linear or branched monovalent hydrocarbon group having one or more carbon-carbon double bond.

As used herein, when a definition is not otherwise provided, “alkoxy” may refer to an alkyl group that is linked via an oxygen (i.e., alkyl-O-), for example methoxy, ethoxy, and sec-butyloxy groups.

As used herein, when a definition is not otherwise provided, “alkylene” may refer to a straight or branched chain, saturated, aliphatic hydrocarbon group having a valence of at least two

As used herein, when a definition is not otherwise provided, “alkynyl” refers to a linear or branched monovalent hydrocarbon group having one or more carbon-carbon triple bond.

As used herein, when a definition is not otherwise provided, “amino group” may refer to a group of the general formula -N(R)₂, wherein each R is independently hydrogen, a C1 to C6 alkyl, or a C6 to C12 aryl.

As used herein, when a definition is not otherwise provided, “arene” may refer to a hydrocarbon having an aromatic ring, and includes monocyclic and polycyclic hydrocarbons wherein the additional ring(s) of the polycyclic hydrocarbon may be aromatic or nonaromatic. Specific arenes include benzene, naphthalene, toluene, and xylene.

As used herein, when a definition is not otherwise provided, “aromatic” refers to an organic compound or group comprising at least one unsaturated cyclic group having delocalized pi electrons. The term encompasses both hydrocarbon aromatic compounds and heteroaromatic compounds.

As used herein, when a definition is not otherwise provided, “aryl” refers to a group formed by removal of at least one hydrogen from an aromatic hydrocarbon (e.g., a phenyl or naphthyl group).

As used herein, when a definition is not otherwise provided, “carbocyclic” may refer to a cyclic group having at least one ring with only carbon atoms in the ring. One or more rings may be present, and each ring may be saturate, unsaturated, or aromatic.

As used herein, when a definition is not otherwise provided, “cycloalkenyl” may refer to a monovalent hydrocarbon group having one or more rings and one or more carbon-carbon double bond in the ring, wherein all ring members are carbon (e.g., cyclopentyl and cyclohexyl).

As used herein, when a definition is not otherwise provided, “cycloalkyl” may refer to a monovalent hydrocarbon group having one or more saturated rings in which all ring members are carbon (e.g., cyclopentyl and cyclohexyl).

As used herein, when a definition is not otherwise provided, “cycloalkynyl” may refer to a stable aliphatic monocyclic or polycyclic group having at least one carbon-carbon triple bond, wherein all ring members are carbon (e.g., cyclohexynyl).

As used herein, when a definition is not otherwise provided, the prefix “halo” may refer to a group or compound including one more of a fluoro, chloro, bromo, iodo, and astatino substituent. A combination of different halo groups (e.g., bromo and fluoro) can be present.

As used herein, when a definition is not otherwise provided, “hetero” refers to one including one or more (e.g., 1 to 3) heteroatom of N, O, S, Si, P, or a combination thereof.

As used herein, when a definition is not otherwise provided, “heteroaryl” may refer to a carbocyclic ring group that has a valence of at least one and includes one or more aromatic rings, in which at least one ring member (e.g., one, two or three ring members) is a heteroatom. In a C3 to C30 heteroaryl, the total number of ring carbon atoms ranges from 3 to 30, with remaining ring atoms being heteroatoms. Multiple rings, if present, may be pendent, spiro or fused. The heteroatom(s) are generally independently nitrogen (N), oxygen (O), P (phosphorus), or sulfur (S).

As used herein, when a definition is not otherwise provided, a “(meth)acryloyl” group is inclusive of an acryloyl group (H₂C═CH—C(═O)—) or a methacryloyl group (H₂C═C(CH₃)—C(═O)—).

As used herein, “Group” refers to a group of Periodic Table.

As used herein, “Group I” may refer to Group IA and Group IB, and examples may include Li, Na, K, Rb, and Cs, but are not limited thereto.

As used herein, “Group II” may refer to Group IIA and Group IIB, and examples of Group II metal may be Cd, Zn, Hg, and Mg, but are not limited thereto.

As used herein, “Group III” may refer to Group IIIA and Group IIIB, and examples of Group III metal may be Al, In, Ga, and Tl, but are not limited thereto.

As used herein, “Group IV” may refer to Group IVA and Group IVB, and examples of a Group IV metal may be Si, Ge, and Sn, but are not limited thereto. As used herein, the term “metal” may include a semi-metal such as Si.

As used herein, “Group V” may refer to Group VA, and examples may include nitrogen, phosphorus, arsenic, antimony, and bismuth, but are not limited thereto.

As used herein, “Group VI” may refer to Group VIA, and examples may include sulfur, selenium, and tellurium, but are not limited thereto.

The quantum efficiency or quantum yield is defined as a ratio of the number of emitted photons divided by the number of absorbed photons. The quantum efficiency or quantum yield may be related to a ratio between photons absorbed and photons emitted through fluorescence. It can be measured in solution or in solid phase. The quantum efficiency or quantum yield can be readily and/or routinely measured using a commercially available measuring equipment (e.g., spectrophotometer) (e.g., Hitachi F-7000 from Hitachi Co., Ltd., a Quantaurus series from Hamamatsu Co. Ltd,, a spectrophotometer manufactured by Horiba Co., Ltd.) in accordance with a manual provided by the manufacturer.

The FWHM and the maximum PL peak wavelength may be determined by a photoluminescent spectrum obtained by a photospectrometer (or Fluorescence Spectrophotometer).

Semiconductor nanocrystal particles (hereinafter, also referred to as quantum dots) may absorb light from an excitation source and may emit light corresponding to an energy bandgap of the quantum dots. The energy bandgap of the quantum dot may vary with a size and a composition thereof. For example, as the size of the quantum dot increases, the quantum dot may have a narrower energy bandgap and may exhibit an increased light emitting wavelength. Semiconductor nanocrystals may be used as a light emitting material in various fields such as a display device, an energy device, or a bio light emitting device.

Quantum dots having relatively increased photoluminescence properties may include cadmium (Cd). Cadmium may cause environmental issues, health issues, or a combination thereof and is a restricted element defined under Restriction of Hazardous Substances Directive (RoHS) in a plurality of countries. Accordingly, there remains a need for development of a cadmium-free quantum dot having improved photoluminescence characteristics.

In order to be applied to, e.g., used in, a quantum dot display device (e.g., including a color conversion layer including the quantum dot) and to realize, e.g., provide, a display device having a relatively high (e.g., about 90 % or greater) color reproducibility under a next generation color standard such as BT2020, a quantum dot having a relatively narrow full width at half maximum (FWHM) is desired. For example, in order for a device to achieve an enhanced color reproducibility under the BT2020 standard, a luminous material used therein may be desired to have a FWHM of less than or equal to about 30 nm.

As the quantum dots according to an embodiment are based on a composition of Zn, Te, and Se and have features that will be described below, and the quantum dots may have a relatively wide band gap and a relatively small Bohr radius e.g., compared to a cadmium based quantum dot or a Group III-V compound based quantum dot, thereby reducing an effect of a particle size distribution thereof on a luminous peak of the quantum dot. The quantum dots of an embodiment do not include cadmium and may emit (e.g., green) light at a desired wavelength with an emission peak having a reduced FWHM. The quantum dot of an embodiment may realize, e.g., exhibit, an improved color reproducibility when applied, e.g., used, in a quantum dot based display device.

In an embodiment, a quantum dot(s) (or a core-shell quantum dot(s)) (hereinafter, which may be referred to simply as “quantum dot”) includes (or include) zinc, selenium, and tellurium. The core-shell quantum dot(s) includes (or include) a core including a first semiconductor nanocrystal material; and a semiconductor nanocrystal shell disposed on (at least a portion of) the core (or a surface thereof). The quantum dot includes aluminum. The quantum dot may not include a toxic heavy metal (e.g., cadmium, lead, or a combination thereof). The quantum dot may not include manganese, copper, or a combination thereof. The quantum dot may not include a Group III-V compound (e.g., an indium phosphide, a gallium phosphide, or a combination thereof). In an X-ray diffraction spectroscopy analysis, the quantum dot may not show, e.g., exhibit, a peak that is assigned to a peak of a Group III-V compound.

In an embodiment, an ultraviolet-visible (UV-Vis) absorption spectrum of the (core-shell) quantum dot may include a valley and an increased value of the valley depth. As used herein, the term “the valley” of the UV-Vis absorption spectrum refers to a portion 2 where a slope of a tangent line of a UV-Vis absorption spectrum curve changes from a negative value to a positive value, as a wavelength increases. The valley may exist near the first absorption peak 1 (see FIG. 1 ).

Without being bound by any theory, it is believed that in ultraviolet-visible (UV-Vis) absorption spectrum, the presence of the valley or the valley depth may represent a size uniformity of a quantum dot (or a core) or shell coating uniformity of the quantum dot. A noticeable valley depth of a core-shell quantum dot or a core quantum dot may indicate that the (core-shell) quantum dot may have an improved size distribution and/or an improved coating quality, which may lead to a narrower FWHM and an increased luminous efficiency.

In an embodiment, a synthesis of the (core or core-shell) quantum dot involves use of an aluminum containing compound (e.g., diisobutylaluminum hydride (DIBAL-H), dimethylethylaminealuminum trihydride (DMEA-AlH₃), LiAlH₄, or the like). The present inventors have found that a UV-Vis absorption spectrum of the quantum dots prepared by the foregoing synthesis may show, e.g., have, a noticeable valley (e.g., a VD thereof). The core-shell quantum dot of an embodiment may exhibit a noticeable valley, which may indicate that a UV-Vis absorption spectrum of the core quantum dot included therein may have a clearly identified valley.

In a UV-vis absorption spectrum of the (core or core-shell) quantum dot, a depth of the valley adjacent to the first absorption peak (i.e., a valley depth (VD)) may be defined by the following equation:

(Abs_(first)- Abs_(valley))/ Abs_(first)= VD

wherein Abs_(first) is an absorption intensity at a wavelength of the first absorption peak and Abs_(valley) is an absorption intensity at a lowest point of the valley.

As used herein, the term “first absorption peak wavelength” refers to a wavelength of a main excitonic peak appearing first from the longest wavelength region of a UV-vis absorption spectrum of a quantum dot (i.e., appearing in the lowest energy region in the UV-Vis absorption spectrum).

In the UV-vis absorption spectrum of the quantum dot, the valley or the lowest point thereof may be appeared at a wavelength lower than the first absorption peak wavelength. In the UV-vis absorption spectrum of the (core or core-shell) quantum dot, the intensity of the first absorption peak may be greater than the intensity at the lowest point of the valley. In the quantum dot of an embodiment, the valley depth (VD) defined above may be greater than or equal to about 0.01, for example, greater than or equal to about 0.02, greater than or equal to about 0.03, greater than or equal to about 0.04, greater than or equal to about 0.05, greater than or equal to about 0.06, greater than or equal to about 0.07, greater than or equal to about 0.08, greater than or equal to about 0.09, greater than or equal to about 0.1, greater than or equal to about 0.11, greater than or equal to about 0.12, greater than or equal to about 0.13, greater than or equal to about 0.14, greater than or equal to about 0.15, greater than or equal to about 0.16, greater than or equal to about 0.17, greater than or equal to about 0.18, or greater than or equal to about 0.19.

The first absorption peak of the quantum dot may be present in a wavelength range of greater than or equal to about 410 nm, for example, greater than or equal to about 420 nm, greater than or equal to about 430 nm, greater than or equal to about 440 nm, greater than or equal to about 450 nm, greater than or equal to about 460 nm, greater than or equal to about 465 nm, greater than or equal to about 470 nm, greater than or equal to about 475 nm, greater than or equal to about 480 nm; and/or less than or equal to about 520 nm, less than or equal to about 530 nm, less than or equal to about 520 nm, less than or equal to about 510 nm, less than or equal to about 505 nm, less than or equal to about 500 nm, less than or equal to about 495 nm, less than or equal to about 490 nm, less than or equal to about 485 nm, less than or equal to about 480 nm, less than or equal to about 475 nm, less than or equal to about 465 nm, less than or equal to about 460 nm, less than or equal to about 455 nm, less than or equal to about 450 nm, or less than or equal to about 445 nm; or a combination thereof.

The lowest point of the valley of the quantum dot may be present in a wavelength range of greater than or equal to about 410 nm, for example, greater than or equal to about 420 nm, greater than or equal to about 430 nm, greater than or equal to about 440 nm, greater than or equal to about 450 nm, greater than or equal to about 460 nm, greater than or equal to about 465 nm, greater than or equal to about 470 nm, greater than or equal to about 475 nm, greater than or equal to about 480 nm; and/or less than or equal to about 530 nm, for example, less than or equal to about 520 nm, less than or equal to about 510 nm, less than or equal to about 505 nm, less than or equal to about 500 nm, less than or equal to about 495 nm, less than or equal to about 490 nm, less than or equal to about 485 nm, less than or equal to about 480 nm, less than or equal to about 475 nm, less than or equal to about 465 nm, less than or equal to about 460 nm, less than or equal to about 455 nm, less than or equal to about 450 nm, less than or equal to about 445 nm; or a combination thereof.

The quantum dot may have a maximum (e.g., photoluminescent) peak wavelength of greater than or equal to about 480 nm, for example, greater than or equal to about 490 nm, greater than or equal to about 495 nm, greater than or equal to about 500 nm, greater than or equal to about 505 nm, greater than or equal to about 510 nm, greater than or equal to about 515 nm, or greater than or equal to about 520 nm; and/or less than or equal to about 550 nm, for example, less than or equal to about 540 nm, less than or equal to about 545 nm, or less than or equal to about 535 nm; or a combination thereof. The quantum dot(s) of an embodiment may emit green light. The green light may have a maximum luminescent peak wavelength of greater than or equal to about 515 nm to about 545 nm.

In comparison with other quantum dots based on Zn, Te, and Se, the quantum dots of an embodiment may emit green light with a significantly improved quantum efficiency, for example, that is greater than or equal to about 5%, greater than or equal to about 6%, greater than or equal to about 7%, greater than or equal to about 8%, greater than or equal to about 9%, greater than or equal to about 10%, greater than or equal to about 11%, greater than or equal to about 12%, greater than or equal to about 13%, greater than or equal to about 14%, greater than or equal to about 15%, greater than or equal to about 16%, greater than or equal to about 17%, greater than or equal to about 18%, greater than or equal to about 19%, or greater than or equal to about 20%.

The (core or core-shell) quantum dots of an embodiment may emit green light having a full width at half maximum of less than or equal to about 50 nm, less than or equal to about 45 nm, less than or equal to about 40 nm, less than or equal to about 35 nm, less than or equal to about 30 nm, less than or equal to about 29 nm, less than or equal to about 28 nm, less than or equal to about 27 nm, less than or equal to about 26 nm, or less than or equal to about 25 nm.

In an embodiment, the quantum dots of an embodiment may have a mole ratio of the tellurium with respect to the selenium that is greater than about 0.05:1, for example, greater than or equal to about 0.055:1, greater than or equal to about 0.06:1, greater than or equal to about 0.065:1, or greater than or equal to about 0.07:1, for example, as determined by an inductively coupled plasma atomic emission spectroscopy analysis (ICP-AES). In the quantum dot, a mole ratio of the tellurium with respect to the selenium may be greater than or equal to about 0.1:1, greater than or equal to about 0.15:1, greater than or equal to about 0.2:1, greater than or equal to about 0.25:1, greater than or equal to about 0.3:1, greater than or equal to about 0.35:1, greater than or equal to about 0.4:1, greater than or equal to about 0.45:1, greater than or equal to about 0.5:1, greater than or equal to about 0.55:1, greater than or equal to about 0.6:1, greater than or equal to about 0.65:1, greater than or equal to about 0.7:1, greater than or equal to about 0.75:1, or greater than or equal to about 0.8:1. In the quantum dot of an embodiment, a mole ratio of the tellurium with respect to the selenium may be greater than 1:1. In the quantum dot of an embodiment, a mole ratio of the tellurium with respect to the selenium may be greater than or equal to about 1:1, greater than or equal to about 1.1:1, greater than or equal to about 1.2:1, greater than or equal to about 1.3:1, greater than or equal to about 1.4:1, greater than or equal to about 1.5:1, greater than or equal to about 1.6:1, greater than or equal to about 1.7:1, greater than or equal to about 1.8:1, greater than or equal to about 1.9:1, greater than or equal to about 2:1, greater than or equal to about 2.1:1, or greater than or equal to about 2.2:1.

In the quantum dot of an embodiment, a mole ratio of the tellurium with respect to the selenium may be less than or equal to about 4:1, less than or equal to about 3.9:1, less than or equal to about 3.8:1, less than or equal to about 3.7:1, less than or equal to about 3.6:1, less than or equal to about 3.5:1, less than or equal to about 3.4:1, less than or equal to about 3.3:1, less than or equal to about 3.2:1, less than or equal to about 3.1:1, less than or equal to about 3:1, less than or equal to about 2.9:1, less than or equal to about 2.8:1, less than or equal to about 2.7:1, less than or equal to about 2.6:1, less than or equal to about 2.5:1, less than or equal to about 2.4:1, less than or equal to about 2.3:1, less than or equal to about 2.2:1, less than or equal to about 2.0:1, less than or equal to about 1.9:1, less than or equal to about 1.8:1, less than or equal to about 1.7:1, less than or equal to about 1.6:1, less than or equal to about 1.5:1, less than or equal to about 1.4:1, or less than or equal to about 1.3:1.

In the quantum dot of an embodiment, a mole ratio of tellurium with respect to zinc (Te:Zn) may be greater than or equal to about 0.02:1, greater than or equal to about 0.03:1, greater than or equal to about 0.1:1, greater than or equal to about 0.12:1, greater than or equal to about 0.13:1, greater than or equal to about 0.14:1, greater than or equal to about 0.15:1, greater than or equal to about 0.16:1, greater than or equal to about 0.17:1, greater than or equal to about 0.18:1, greater than or equal to about 0.19:1, greater than or equal to about 0.2:1, greater than or equal to about 0.21:1, greater than or equal to about 0.22:1, greater than or equal to about 0.23:1, greater than or equal to about 0.24:1, greater than or equal to about 0.25:1, greater than or equal to about 0.26:1, greater than or equal to about 0.27:1, or greater than or equal to about 0.28:1, for example, as determined by an inductively coupled plasma atomic emission spectroscopy analysis (ICP-AES).

In the quantum dot of an embodiment, a mole ratio of tellurium with respect to zinc (Te:Zn) may be less than or equal to about 0.5:1, less than or equal to about 0.45:1, less than or equal to about 0.4:1, less than or equal to about 0.35:1, or less than or equal to about 0.3:1, for example, as determined by an inductively coupled plasma atomic emission spectroscopy analysis (ICP-AES).

In the quantum dot of an embodiment, a mole ratio of sulfur with respect to zinc (S:Zn) may be greater than or equal to about 0.1:1 and less than or equal to about 0.6:1.

The core may include a first semiconductor nanocrystal that includes zinc, selenium, and tellurium. The core may include ZnTe_(x)Se_(1-x), wherein x is greater than or equal to about 0.5, for example, greater than or equal to about 0.51, greater than or equal to about 0.52, greater than or equal to about 0.53, greater than or equal to about 0.54, greater than or equal to about 0.55, greater than or equal to about 0.56, greater than or equal to about 0.57, greater than or equal to about 0.58, greater than or equal to about 0.59, greater than or equal to about 0.6, greater than or equal to about 0.61, greater than or equal to about 0.62, greater than or equal to about 0.63, greater than or equal to about 0.64, greater than or equal to about 0.65, greater than or equal to about 0.66, greater than or equal to about 0.67, greater than or equal to about 0.68, greater than or equal to about 0.69, greater than or equal to about 0.70, greater than or equal to about 0.71, greater than or equal to about 0.72, greater than or equal to about 0.73, greater than or equal to about 0.74, or greater than or equal to about 0.75 and less than or equal to about 0.9, less than or equal to about 0.89, less than or equal to about 0.88, less than or equal to about 0.87, less than or equal to about 0.86, less than or equal to about 0.85, less than or equal to about 0.84, less than or equal to about 0.83, less than or equal to about 0.82, or less than or equal to about 0.8.

In the core quantum dot (or the first semiconductor nanocrystal) or in the core-shell quantum dot, an amount of tellurium may be greater than that of selenium.

In an embodiment, the core or the first semiconductor nanocrystal may have a mole ratio of selenium with respect to tellurium that is greater than or equal to about 0.1:1, greater than or equal to about 0.2, :1 greater than or equal to about 0.3:1, greater than or equal to about 0.31:1, greater than or equal to about 0.34:1, greater than or equal to about 0.4:1, greater than or equal to about 0.43:1, greater than or equal to about 0.45:1, or greater than or equal to about 0.5:1 and/or less than or equal to about 1.5:1, less than or equal to about 1:1, less than or equal to about 0.95:1, less than or equal to about 0.9:1, less than or equal to about 0.8:1, less than or equal to about 0.65:1, or less than or equal to about 0.7:1.

The core-shell quantum dot (e.g., the first semiconductor nanocrystal or the core quantum dot) may further include aluminum. The core-shell quantum dot (e.g., the first semiconductor nanocrystal or the core quantum dot) may further include lithium. The semiconductor nanocrystal shell may not include aluminum, lithium, or a combination thereof.

In the core-shell quantum dot, the core quantum dot, or the first semiconductor nanocrystal, a mole ratio of aluminum with respect to tellurium may be greater than or equal to about 0.01:1, for example, greater than or equal to about 0.02:1, greater than or equal to about 0.03, greater than or equal to about 0.04:1, greater than or equal to about 0.05, greater than or equal to about 0.06:1, greater than or equal to about 0.07, greater than or equal to about 0.08:1, greater than or equal to about 0.09, greater than or equal to about 0.1:1, greater than or equal to about 0.11:1, greater than or equal to about 0.12:1, greater than or equal to about 0.13:1, greater than or equal to about 0.14:1, greater than or equal to about 0.15:1, greater than or equal to about 0.16:1, greater than or equal to about 0.17:1, greater than or equal to about 0.18:1, greater than or equal to about 0.19:1, greater than or equal to about 0.2:1, greater than or equal to about 0.21:1, greater than or equal to about 0.22:1, greater than or equal to about 0.23:1, greater than or equal to about 0.24:1, greater than or equal to about 0.25:1, greater than or equal to about 0.26:1, greater than or equal to about 0.27:1, greater than or equal to about 0.28:1, greater than or equal to about 0.29:1, greater than or equal to about 0.3:1, greater than or equal to about 0.31:1, greater than or equal to about 0.32:1, greater than or equal to about 0.33:1, greater than or equal to about 0.34:1, greater than or equal to about 0.35:1, greater than or equal to about 0.36:1, greater than or equal to about 0.37:1, greater than or equal to about 0.38:1, greater than or equal to about 0.39:1, greater than or equal to about 0.4:1, greater than or equal to about 0.41:1, greater than or equal to about 0.42:1, greater than or equal to about 0.43:1, greater than or equal to about 0.44:1, greater than or equal to about 0.45:1, greater than or equal to about 0.46:1, greater than or equal to about 0.47:1, greater than or equal to about 0.48, greater than or equal to about 0.49:1, or greater than or equal to about 0.50:1.

In the core-shell quantum dot (e.g., in the first semiconductor nanocrystal) or the core quantum dot, a mole ratio of aluminum with respect to tellurium may be less than or equal to about 1:1, for example, less than or equal to about 0.9:1, less than or equal to about 0.85:1, less than or equal to about 0.8:1, less than or equal to about 0.7:1, less than or equal to about 0.6:1, less than or equal to about 0.5:1, less than or equal to about 0.4:1, or less than or equal to about 0.3:1.

In case where the core-shell quantum dot (e.g., in the first semiconductor nanocrystal) or the core quantum dot further include lithium, a mole ratio of lithium with respect to tellurium may be greater than or equal to about 0.01:1, greater than or equal to about 0.02:1, greater than or equal to about 0.03:1, greater than or equal to about 0.04:1, greater than or equal to about 0.05:1, greater than or equal to about 0.06:1, greater than or equal to about 0.07:1, greater than or equal to about 0.08:1, greater than or equal to about 0.09:1, greater than or equal to about 0.1:1, greater than or equal to about 0.15:1, greater than or equal to about 0.2:1, greater than or equal to about 0.3:1, greater than or equal to about 0.4:1, or greater than or equal to about 0.5:1 and less than or equal to about 1:1, for example, less than or equal to about 0.9:1, less than or equal to about 0.8:1, less than or equal to about 0.7:1, less than or equal to about 0.6:1, less than or equal to about 0.5:1, less than or equal to about 0.4:1, less than or equal to about 0.3:1, less than or equal to about 0.2:1, less than or equal to about 0.15:1, or less than or equal to about 0.1:1.

In a quantum dot of an embodiment, the semiconductor nanocrystal shell includes zinc (Zn), and at least one of selenium (Se), and sulfur (S). The semiconductor nanocrystal shell may include, e.g., be, ZnSe, ZnS, ZnSeS, or a combination thereof. The semiconductor nanocrystal shell may be a multi-layered shell including a plurality of layers. In the plurality of layers for the shell, adjacent layers may have semiconductor nanocrystal material of different compositions. The multi-layered shell may include a first layer disposed directly on the core and a second layer disposed on or over the first layer. The first layer may include a second semiconductor nanocrystal. The second layer may include a third semiconductor nanocrystal having a composition different from the second semiconductor nanocrystal. The second layer may be the outermost layer of the core-shell quantum dot. The second semiconductor nanocrystal may include zinc, selenium, and optionally sulfur. The second semiconductor nanocrystal may not include sulfur. The third semiconductor nanocrystal may include zinc and sulfur. The third semiconductor nanocrystal may not include selenium.

In a multi-layered shell, a thickness of each layer may be selected appropriately. The thickness of the layer may be greater than or equal to about 1 monolayer (ML), for example, greater than or equal to about 2 ML, greater than or equal to about 3 ML, greater than or equal to about 4 ML, greater than or equal to about 5 ML and less than or equal to about 10 ML, for example, less than or equal to about 9 ML, less than or equal to about 8 ML, less than or equal to about 7 ML, less than or equal to about 6 ML, or less than or equal to about 5 ML. The thickness of each layer in the multi-layered shell may be selected taking into consideration a desired composition of a final quantum dot.

In an embodiment, the quantum dot may include a ZnSe layer a ZnSeS layer, a ZnS layer, or a combination thereof, each of which may be disposed directly on the core. An outermost layer of the quantum dot may include (or consist of) ZnS.

In the shell or the multi-layered shell, each of the layer may include a gradient alloy having a composition varying in a direction of a radius, e.g., a radial direction from the core toward an outermost surface of the core-shell quantum dot. In an embodiment, an amount of the sulfur in the semiconductor nanocrystal shell may increase toward a surface of the core-shell quantum dot. For example, in the shell, the amount of the sulfur may increase in a direction away from the core, e.g., in a radial direction from the core toward an outermost surface of the core-shell quantum dot.

The core-shell quantum dot may include various shapes. The shape of the core-shell quantum dot may include a spherical shape, a polygonal shape, a multipod shape, or a combination thereof. The (cadmium free) quantum dot may show a cubic Zinc Blende crystalline structure for example when analyzed by an X-ray diffraction. Diffraction peaks of the (cadmium free) quantum dot may be indexed to the cubic structure in agreement with the Joint Committee on Powder Diffraction Standard cards.

A size (or an average size) of the core(s) may be greater than or equal to about 1 nm, for example, greater than or equal to about 2 nm, greater than or equal to about 3 nm or greater than or equal to about 3.5 nm. A size (or an average size) of the core(s) may be less than or equal to about 5 nm, for example, less than or equal to about 4 nm. As used herein, the size of the quantum dot may refer to a diameter or an equivalent diameter obtained from a two-dimensional image of an electron microscopy analysis (e.g., under an assumption of a circle).

The (core-shell) quantum dot(s) may have a particle (average) size of greater than or equal to about 2 nm, greater than or equal to about 3 nm, greater than or equal to about 4 nm, greater than or equal to about 5 nm, greater than or equal to about 6 nm, greater than or equal to about 7 nm, or greater than or equal to about 8 nm. A size (or an average size) of the quantum dot (or a population thereof) may be less than or equal to about 50 nm, for example, less than or equal to about 45 nm, less than or equal to about 40 nm, less than or equal to about 35 nm, less than or equal to about 30 nm, less than or equal to about 25 nm, less than or equal to about 24 nm, less than or equal to about 23 nm, less than or equal to about 22 nm, less than or equal to about 21 nm, less than or equal to about 20 nm, less than or equal to about 19 nm, less than or equal to about 18 nm, less than or equal to about 17 nm, less than or equal to about 16 nm, less than or equal to about 15 nm, less than or equal to about 14 nm, less than or equal to about 13 nm, less than or equal to about 12 nm, less than or equal to about 11 nm, or less than or equal to about 10 nm.

The quantum dot(s) may constitute a population of quantum dots. The aforementioned population of the quantum dots may have a standard deviation of sizes that is less than or equal to about 15%, for example, less than or equal to about 14%, less than or equal to about 13%, less than or equal to about 12%, or less than or equal to about 11%.

The quantum dot may include an organic ligand e.g., on a surface thereof. The organic ligand may include RCOOH, RNH₂, R₂NH, R₃N, RSH, RH₂PO, R₂HPO, R₃PO, RH₂P, R₂HP, R₃P, ROH, RCOOR′, RPO(OH)₂, RHPOOH, R₂POOH, a polymeric organic ligand, or a combination thereof wherein R and R′ are the same or different, and are independently a C1 to C40 (e.g., C3 to C30 or C6 to C24) substituted or unsubstituted aliphatic hydrocarbon (alkyl, alkenyl, or alkynyl) group or a C6 to C40 substituted or unsubstituted aromatic hydrocarbon group, or a combination thereof. The organic ligand may be used alone or as a mixture of at least two compounds.

The organic ligand may coordinate to, e.g., be bound to, the surface of the quantum dot, helping the nanocrystal to be well dispersed in the solution. Examples of the organic ligand may include methane thiol, ethane thiol, propane thiol, butane thiol, pentane thiol, hexane thiol, octane thiol, dodecane thiol, hexadecane thiol, octadecane thiol, or benzyl thiol; methyl amine, ethyl amine, propyl amine, butyl amine, pentyl amine, hexyl amine, octyl amine, dodecyl amine, hexadecyl amine, octadecyl amine, dimethyl amine, diethyl amine, dipropyl amine; methanoic acid, ethanoic acid, propanoic acid, butanoic acid, pentanoic acid, hexanoic acid, heptanoic acid, octanoic acid, dodecanoic acid, hexadecanoic acid, octadecanoic acid, oleic acid, or benzoic acid; a phosphine such as a substituted or unsubstituted methyl phosphine (e.g., trimethyl phosphine, methyldiphenyl phosphine, etc.), a substituted or unsubstituted ethyl phosphine (e.g., triethyl phosphine, ethyldiphenyl phosphine, etc.), a substituted or unsubstituted propyl phosphine, a substituted or unsubstituted butyl phosphine, a substituted or unsubstituted pentyl phosphine, or a substituted or unsubstituted octylphosphine (e.g., trioctylphosphine (TOP)); a phosphine oxide such as substituted or unsubstituted methyl phosphine oxide (e.g., trimethyl phosphine oxide, methyldiphenyl phosphine oxide, etc.), a substituted or unsubstituted ethyl phosphine oxide (e.g., triethyl phosphine oxide, ethyldiphenyl phosphine oxide, etc.), a substituted or unsubstituted propyl phosphine oxide, a substituted or unsubstituted butyl phosphine oxide, or a substituted or unsubstituted octyl phosphine oxide (e.g., trioctylphosphine oxide (TOPO)); diphenyl phosphine, diphenyl phosphine oxide, triphenyl phosphine, triphenyl phosphine oxide; a mono- or di(C5 to C20 alkyl)phosphinic acid such as mono- or di(hexyl)phosphinic acid, mono- or dioctylphosphinic acid, mono- or di(dodecyl)phosphinic acid, mono- or di(tetradecyl)phosphinic acid, mono- or di(hexadecyl)phosphinic acid, mono- or di(octadecyl)phosphinic acid, or a combination thereof; a C5 to C20 alkylphosphinic acid, a C5 to C20 alkylphosphonic acid such as hexylphosphonic acid, octylphosphonic acid, dodecylphosphonic acid, tetradecylphosphonic acid, hexadecylphosphonic acid, octadecylphosphonic acid, or a combination thereof; and the like, but are not limited thereto. Two or more different organic ligand compounds may be used. In an embodiment, the organic ligand compound may be a combination of RCOOH and an amine (e.g., RNH₂, R₂NH, R₃N, or a combination thereof). In an embodiment the organic ligand may not include an organic compound having, e.g., including, a thiol moiety and at least one of an amino group, a carboxylic acid group, or a combination thereof. For example, the organic ligand may not include glutathione compound. In an embodiment, the quantum dot may be water insoluble.

In an embodiment, the quantum dot may have a core structure not having a shell (e.g., an inorganic shell). In this case, the quantum dot (i.e., the core quantum dot) includes zinc, tellurium, and selenium, and the quantum dot includes aluminum and does not include cadmium, and in the quantum dot, an amount of the aluminum with respect to one mole of tellurium may be greater than or equal to about 0.01.

In the (core of the) quantum dot, an amount of tellurium with respect to selenium may be the same as set forth above about the first semiconductor nanocrystal or the core. The quantum dot may not include manganese, copper, or a combination thereof. The quantum dot may not include a Group III-V compound. The quantum dot may be configured to emit light having a FWHM of less than or equal to about 40 nm. Details set forth above for the core-shell quantum dot or the first semiconductor nanocrystal may be applied to the (core of the) quantum dot.

In an embodiment, a method of manufacturing the foregoing quantum dot(s) includes

-   synthesizing a core particle (hereinafter, be referred to simply as     “core,” as well) including a first semiconductor nanocrystal     including zinc, selenium, and tellurium; -   in an organic solvent, in the presence of the core particle and an     organic ligand, reacting a zinc precursor and a selenium precursor,     a sulfur precursor, or a combination thereof at a shell formation     temperature (e.g., in a plurality of steps) to form a semiconductor     nanocrystal shell including zinc, selenium, and sulfur on a surface     of the core, -   wherein the method includes injecting an aluminum compound during     the synthesis of the core particle.

Details for the core (particle) may be the same as set forth above (e.g., example a first semiconductor nanocrystal).

In an embodiment, the synthesis of the core may include preparing a zinc organic solution including a zinc precursor in an organic solvent and a first organic ligand, preparing a selenium precursor and a tellurium precursor; during a heating of the zinc organic solution at a core formation temperature, injecting the selenium precursor and the tellurium precursor thereto together with the aluminum compound and optionally a, e.g., at least one (e.g., at least two), second organic ligand to conduct a reaction therebetween. The cores as synthesized may be removed (separated) from a reaction system (e.g., via addition of a non-solvent). Separation using the non-solvent will be described in detail below. In an embodiment, formation of the shell may be carried out by heating (or vacuum treating) a shell metal precursor and an organic ligand in an organic solvent at a predetermined temperature (e.g., at a temperature of greater than or equal to about 100° C., for example, greater than or equal to about 120° C.), changing an atmosphere of a reaction system into an inert gas and heating the same at a predetermined reaction temperature. The core and a non-metal shell precursor (e.g., sulfur and selenium precursors) may be added to the reaction system to carry out a reaction therebetween to form a shell on the core. The shell precursor(s) may be injected at the same time or sequentially during the reaction taking into consideration a desired shell composition.

The shell has a gradient composition or a multi-layered composition.

In an embodiment, a zinc precursor may be reacted with a selenium precursor to form a first layer including zinc and selenium and then reacted with a sulfur precursor to form a second layer including zinc and sulfur. The semiconductor nanocrystal shell formation may include reacting the zinc precursor and the selenium precursor. The semiconductor nanocrystal shell formation may include reacting the zinc precursor and the sulfur precursor. The semiconductor nanocrystal shell formation may include reacting the zinc precursor with the selenium precursor and then reacting the zinc precursor with the sulfur precursor.

In the foregoing method, the zinc precursor may include a Zn powder, ZnO, an alkylated Zn compound (e.g., C2 to C30 alkyl (e.g., dialkyl) zinc such as dimethyl zinc, diethyl zinc), a Zn alkoxide (e.g., a zinc ethoxide), a Zn carboxylate (e.g., a zinc acetate or zinc aliphatic carboxylate, for example, zinc long chain aliphatic carboxylate such as zinc oleate), a Zn nitrate, a Zn perchlorate, a Zn sulfate, a Zn acetylacetonate, a Zn halide (e.g., a zinc chloride), a Zn cyanide, a Zn hydroxide, zinc carbonate, zinc peroxide, or a combination thereof. Examples of the zinc precursor may include dimethyl zinc, diethyl zinc, zinc acetate, zinc acetylacetonate, zinc iodide, zinc bromide, zinc chloride, zinc fluoride, zinc carbonate, zinc cyanide, zinc nitrate, zinc oxide, zinc peroxide, zinc perchlorate, zinc sulfate, or a combination thereof.

The selenium precursor may include selenium-trioctylphosphine (Se-TOP), selenium-tributylphosphine (Se-TBP), selenium-triphenylphosphine (Se-TPP), selenium-diphenylphosphine (Se-DPP), or a combination thereof, but is not limited thereto.

The tellurium precursor may include tellurium-trioctylphosphine (Te-TOP), tellurium-tributylphosphine (Te-TBP), tellurium-triphenylphosphine (Te-TPP), tellurium-diphenylphosphine (Te-DPP), or a combination thereof, but is not limited thereto.

The sulfur precursor may include hexane thiol, octane thiol, decane thiol, dodecane thiol, hexadecane thiol, mercapto propyl silane, sulfur-trioctylphosphine (S-TOP), sulfur-tributylphosphine (S-TBP), sulfur-triphenylphosphine (S-TPP), sulfur-trioctylamine (S-TOA), bistrimethylsilyl sulfide, ammonium sulfide, sodium sulfide, or a combination thereof.

The zinc precursor solution may include at least two kinds of organic ligands in an organic solvent. The at least two kinds of organic ligands may include fatty acid and amine compounds. In a zinc precursor solution, a concentration of the zinc precursor and a concentration of the organic ligand are not particularly limited and may be selected appropriately.

The selenium precursor may include selenium-trioctylphosphine (Se-TOP), selenium-tributylphosphine (Se-TBP), selenium-triphenylphosphine (Se-TPP), selenium-diphenylphosphine (Se-DPP), or a combination thereof, but is not limited thereto. The tellurium precursor may include tellurium-trioctylphosphine (Te-TOP), tellurium-tributylphosphine (Te-TBP), tellurium-triphenylphosphine (Te-TPP), or a combination thereof, but is not limited thereto.

The organic solvent may be a C6 to C22 primary amine such as a hexadecylamine, a C6 to C22 secondary amine such as dioctylamine, a C6 to C40 tertiary amine such as a trioctyl amine, a nitrogen-containing heterocyclic compound such as pyridine, a C6 to C40 olefin such as octadecene, a C6 to C40 aliphatic hydrocarbon such as hexadecane, octadecane, or squalane, an aromatic hydrocarbon substituted with a C6 to C30 alkyl group such as phenyldodecane, phenyltetradecane, or phenyl hexadecane, a primary, secondary, or tertiary phosphine (e.g., trioctyl phosphine) substituted with at least one (e.g., 1, 2, or 3) C6 to C22 alkyl group, a phosphine oxide (e.g., trioctylphosphine oxide) substituted with at least one (e.g., 1, 2, or 3) C6 to C22 alkyl group, a C12 to C22 aromatic ether such as a phenyl ether or a benzyl ether, or a combination thereof.

The first organic ligand and the second organic ligand may be the same. The first organic ligand and the second organic ligand may be different. Details for the first and the second organic ligands are the same as set forth above about the organic ligand. In an embodiment, the first organic ligand may include a fatty acid (e.g., including a C5 or greater or C10 or greater aliphatic hydrocarbon group) and the second organic ligand may include a fatty organic (e.g., primary) amine (e.g., including a C5 or greater or C10 or greater aliphatic hydrocarbon group), an aromatic phosphine compound, or a combination thereof.

The aluminum compound may include an organic compound including aluminum and hydrogen (e.g., together with carbon), an inorganic compound including aluminum and hydrogen, or a combination thereof. In an embodiment, the aluminum compound may include alkyl aluminum hydride (e.g., diisobutyl aluminum hydride), a Lewis base complex of an aluminum hydride (e.g., AlH₃·NMe₂Et, AlH₃·NMe₃ and AlH₃·nEt₂O, wherein Me is methyl and Et is ethyl), lithium aluminum hydride, or a combination thereof. The aluminum compound may include an alkoxy substituted aluminum hydride such as lithium tri-tert-butoxyaluminum hydride, sodium bis(2-methoxyethoxy)aluminum hydride, or the like.

In an embodiment, the aluminum compound may include an inorganic compound having aluminum and hydride (e.g., not including carbon).

In an embodiment, the selenium precursor, the tellurium precursor, the aluminum compound may be injected into the zinc organic solution optionally together with the organic ligand. In an embodiment, prior to being added to the zinc organic solution, the tellurium precursor, the aluminum compound, and the second organic ligand may be mixed into a single stock solution at a temperature of less than or equal to about 80° C., for example, less than or equal to about 75° C., less than or equal to about 70° C., less than or equal to about 65° C., less than or equal to about 60° C., less than or equal to about 55° C., less than or equal to about 50° C., or less than or equal to about 45° C.

In an embodiment, the selenium precursor, the tellurium precursor, and the aluminum compound may be injected into the zinc organic solution sequentially.

The reaction temperature for the core formation may be greater than or equal to about 250° C., greater than or equal to about 260° C., greater than or equal to about 270° C., greater than or equal to about 280° C., greater than or equal to about 290° C., or greater than or equal to about 300° C. The reaction temperature for the core formation may be less than or equal to about 350° C., for example, less than or equal to about 340° C., less than or equal to about 330° C., less than or equal to about 320° C., or less than or equal to about 310° C. The reaction time for the core formation is not particularly limited and may be selected appropriately.

The reaction temperature for the shell formation may be selected appropriately in any suitable range of greater than or equal to about 200° C., for example, greater than or equal to about 210° C., greater than or equal to about 220° C., greater than or equal to about 230° C., greater than or equal to about 240° C., greater than or equal to about 250° C., greater than or equal to about 260° C., greater than or equal to about 270° C., greater than or equal to about 280° C., or greater than or equal to about 290° C. and less than or equal to about 340° C., for example, less than or equal to about 325° C. The reaction time for the shell formation may be selected appropriately in light of a desired shell composition.

In a reaction system for the core formation and a reaction system for the shell formation, an amount of each precursor and a concentration thereof may be selected taking into consideration a desired composition of the core and the shell, a reactivity between the core and shell precursors, or the like. In an embodiment, taking into consideration a desired composition of a final quantum dot (e.g., a ratio between elements such as Zn, S, Se, Te, or a combination thereof), ratios between the precursors may be controlled. The composition of the final quantum dot may be determined by an appropriate analysis tool such as an inductively coupled plasma atomic emission spectroscopy.

After the formation of the core, the shell, or a combination thereof, a non-solvent is added to reaction products and the nanocrystal particles coordinated with, e.g., bound to, the ligand compound may be separated. The non-solvent may be a polar solvent that is miscible with the solvent used in the core formation, shell formation, or a combination thereof and may not be capable of dispersing the produced nanocrystals therein. The non-solvent may be selected taking into consideration the solvent used in the reaction and may be for example acetone, ethanol, butanol, isopropanol, ethanediol, water, tetrahydrofuran (THF), dimethylsulfoxide (DMSO), diethylether, formaldehyde, acetaldehyde, a solvent having a similar solubility parameter to the foregoing solvents, or a combination thereof. Separation of the nanocrystal particles may involve centrifugation, sedimentation, chromatography, or distillation. The separated nanocrystal particles may be added to a washing (or dispersing) solvent and washed (or dispersed), if desired. Types of the washing (dispersing) solvent are not particularly limited and a solvent having similar solubility parameter to that of the ligand may be used and examples thereof may include hexane, heptane, octane, chloroform, toluene, benzene, or the like.

The core-shell quantum dots of an embodiment may not dispersible in water, the foregoing listed non-solvent, or a combination thereof. The core-shell quantum dots of an embodiment may be water-insoluble. The core-shell quantum dots of an embodiment may be dispersed the aforementioned organic solvent. In an embodiment, the core-shell quantum dots may be dispersed in a C6 to C40 aliphatic hydrocarbon, a C6 to C40 aromatic hydrocarbon, or a combination thereof.

In an embodiment, a composition includes the aforementioned (e.g., a plurality of) (core-shell) quantum dot(s) (hereinafter, may be referred to simply as quantum dot or quantum dots); and a dispersing agent (e.g., a binder monomer or polymer); a polymerizable monomer having a, e.g., at least one, carbon-carbon double bond; a (photo) initiator, or a combination thereof. The binder monomer or polymer may include a carboxylic acid group. The composition may further include an organic solvent, a liquid vehicle, or a combination thereof.

The composition according to an embodiment may be prepared by a method including: preparing a quantum dot dispersion including the aforementioned quantum dot, the dispersing agent, and the organic solvent; and mixing the quantum dot dispersion with the initiator, the polymerizable monomer (e.g., acryl-based monomer), optionally the thiol compound; optionally the metal oxide particulate, and optionally the additives. Each of the aforementioned components may be mixed sequentially or simultaneously, but mixing orders are not particularly limited.

The composition thus prepared may provide a quantum dot-polymer composite via a (e.g., radical) polymerization. Thus, in an embodiment, a quantum dot-polymer composite includes a polymer matrix; and the aforementioned quantum dot(s) dispersed in the polymer matrix. The polymer matrix may include a dispersing agent (e.g., a binder monomer or polymer including a carboxylic acid group), a polymerization product (e.g., an insulating polymer) of an ene compound, i.e., a polymerizable monomer having a carbon-carbon double bond (at least one, for example, at least two, at least three, at least four, or at least five carbon-carbon double bonds), optionally a polymerization product of the polymerizable monomer and a thiol compound including at least one thiol group (e.g., at a terminal end of the thiol compound), preferably a multi-functional thiol compound including at least one, preferably at least two thiol groups (e.g., at a terminal end of the multi-functional thiol compound), a metal oxide particulate(s), or a combination thereof.

In an embodiment, the polymer matrix may include a cross-linked polymer and a dispersing agent (e.g., a carboxylic acid group-containing binder polymer). In an embodiment, the polymer matrix does not include a conjugated polymer (except for a cardo resin). The cross-linked polymer may include a thiolene resin, a cross-linked poly(meth)acrylate, or a combination thereof. In an embodiment, the cross-linked polymer may be a polymerization product of the ene compound (the polymerizable monomer) and, optionally, the multi-functional thiol compound.

An amount of the quantum dot(s) in the composition (or the composite) may be appropriately adjusted taking into consideration a desirable final use (e.g., a photoluminescent color filter, etc.). In an embodiment, the amount of the quantum dot may be greater than or equal to about 1 weight percent (wt%), for example, greater than or equal to about 2 wt%, greater than or equal to about 3 wt%, greater than or equal to about 4 wt%, greater than or equal to about 5 wt%, greater than or equal to about 6 wt%, greater than or equal to about 7 wt%, greater than or equal to about 8 wt%, greater than or equal to about 9 wt%, greater than or equal to about 10 wt%, greater than or equal to about 15 wt%, greater than or equal to about 20 wt%, greater than or equal to about 25 wt%, greater than or equal to about 30 wt%, greater than or equal to about 35 wt%, or greater than or equal to about 40 wt%, based on a total solids content of the composition. The amount of the quantum dot may be less than or equal to about 70 wt%, for example, less than or equal to about 65 wt%, less than or equal to about 60 wt%, less than or equal to about 55 wt%, or less than or equal to about 50 wt%, based on a total solids content of the composition.

The composition according to an embodiment may be used to produce a quantum dot-polymer composite pattern. The composition according to an embodiment may be a quantum dot-containing photoresist composition to which a photolithography method may be applied. The composition according to an embodiment may be an ink composition that may provide a pattern by printing (e.g., a droplet discharge method such as inkjet printing).

In the composition or the composite according to an embodiment, a dispersing agent may ensure dispersion of the quantum dot(s). In an embodiment, the dispersing agent may be a binder monomer or polymer. The binder monomer or polymer may include a carboxylic acid group.

The binder polymer may include a copolymer of a monomer mixture including a first monomer including a carboxylic acid group and a carbon-carbon double bond, a second monomer including a carbon-carbon double bond and a hydrophobic moiety and not including a carboxylic acid group, and optionally a third monomer including a carbon-carbon double bond and a hydrophilic moiety and not including a carboxylic acid group;

-   a multiple aromatic ring-containing polymer having a backbone     structure in which two aromatic rings are bound to a quaternary     carbon atom that is a constituent atom of another cyclic moiety in     the main chain and including a carboxylic acid group (—COOH)     (hereinafter, a cardo binder); or -   a combination thereof.

The copolymer includes a first repeating unit derived from the first monomer and a second repeating unit derived from the second monomer, and optionally a third repeating unit derived from the third monomer.

Examples of the first monomer may include carbonic acid (i.e., carboxylic acid) vinyl ester compounds such as acrylic acid, methacrylic acid, maleic acid, itaconic acid, fumaric acid, 3-butenoic acid, but are not limited thereto. One or more first monomers may be used. Examples of the second monomer may be an alkenyl aromatic compound such as styrene, alpha-methyl styrene, vinyl toluene, vinyl benzoate, or vinyl benzyl methyl ether; an unsaturated carbonic acid ester compound such as vinyl acetate, methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, butyl acrylate, butyl methacrylate, benzyl acrylate, benzyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate, phenyl acrylate, or phenyl methacrylate; an unsaturated carbonic acid amino alkyl ester compound such as 2-amino ethyl acrylate, 2-amino ethyl methacrylate, 2-dimethyl amino ethyl acrylate, or 2-dimethyl amino ethyl methacrylate; a maleimide such as N-phenylmaleimide, N-benzylmaleimide, N-alkylmaleimide; an unsaturated carbonic acid glycidyl ester compound such as glycidyl acrylate or glycidyl methacrylate; a vinyl cyanide compound such as acrylonitrile, methacrylonitrile; or a unsaturated amide compound such as acryl amide or methacryl amide, but are not limited thereto. One or more second monomers may be used. Specific examples of the third monomer may include 2-hydroxy ethyl acrylate, 2-hydroxy ethyl methacrylate, 2-hydroxy butyl acrylate, or 2-hydroxy butyl methacrylate, but are not limited thereto. One or more third monomers may be used.

In the carboxylic acid group-containing polymer (also referred to as a binder or a binder polymer), the content of each of the first repeating unit or the second repeating unit may independently be greater than or equal to about 10 mole percent (mol%), for example, greater than or equal to about 15 mol%, greater than or equal to about 25 mol%, or greater than or equal to about 35 mol%, based on a total number of moles in the carboxylic acid group containing polymer. In the carboxylic acid group containing polymer, an amount of the first repeating unit or the second repeating unit may be less than or equal to about 90 mol%, for example, 89 mol%, less than or equal to about 80 mol%, less than or equal to about 70 mol%, less than or equal to about 60 mol%, less than or equal to about 50 mol%, less than or equal to about 40 mol%, less than or equal to about 35 mol%, or less than or equal to about 25 mol%, based on a total number of moles in the carboxylic acid group containing polymer. In the carboxylic acid group containing polymer, if present, an amount of the third repeating unit may be greater than or equal to about 1 mol%, for example, greater than or equal to about 5 mol%, greater than or equal to about 10 mol%, or greater than or equal to about 15 mol%, based on a total number of moles in the carboxylic acid group containing polymer. In the binder polymer, an amount of the third repeating unit may be less than or equal to about 30 mol%, for example, less than or equal to about 25 mol%, less than or equal to about 20 mol%, less than or equal to about 18 mol%, less than or equal to about 15 mol%, or less than or equal to about 10 mol%, based on a total number of moles in the binder polymer.

The carboxylic acid group-containing polymer may include a multiple aromatic ring-containing polymer. The multiple aromatic ring-containing polymer is known as a cardo binder resin and may commercially available.

The carboxylic acid group-containing polymer may have an acid value of greater than or equal to about 50 milligrams of potassium hydroxide per gram (mg KOH/g). For example, the carboxylic acid group containing polymer may have an acid value of greater than or equal to about 60 mg KOH/g, greater than or equal to about 70 mg KOH/g, greater than or equal to about 80 mg KOH/g, greater than or equal to about 90 mg KOH/g, greater than or equal to about 100 mg KOH/g, greater than or equal to about 110 mg KOH/g, greater than or equal to about 120 mg KOH/g, greater than or equal to about 125 mg KOH/g, or greater than or equal to about 130 mg KOH/g. The acid value of the carboxylic acid group-containing polymer may be for example less than or equal to about 250 mg KOH/g, for example, less than or equal to about 240 mg KOH/g, less than or equal to about 230 mg KOH/g, less than or equal to about 220 mg KOH/g, less than or equal to about 210 mg KOH/g, less than or equal to about 200 mg KOH/g, less than or equal to about 190 mg KOH/g, less than or equal to about 180 mg KOH/g, or less than or equal to about 160 mg KOH/g, but is not limited thereto. The binder polymer may have a weight average molecular weight of greater than or equal to about 1,000 grams per mole (g/mol), for example, greater than or equal to about 2,000 g/mol, greater than or equal to about 3,000 g/mol, or greater than or equal to about 5,000 g/mol. The binder polymer may have a weight average molecular weight of less than or equal to about 100,000 g/mol, for example less than or equal to about 50,000 g/mol.

In the composition, an amount of the dispersing agent or the binder (polymer or monomer) may be greater than or equal to about 0.5 wt%, for example, greater than or equal to about 1 wt%, greater than or equal to about 5 wt%, greater than or equal to about 10 wt%, greater than or equal to about 15 wt%, or greater than or equal to about 20 wt%, based on a total weight of the composition, but is not limited thereto. The amount of the binder polymer may be less than or equal to about 55 wt%, less than or equal to about 45 wt%, less than or equal to about 35 wt%, for example less than or equal to about 33 wt%, or less than or equal to about 30 wt%, based on a total weight of the composition or on a total weight of solids in the composition. The aforementioned amount of the dispersing agent may provide enhanced dispersibility of the quantum dots.

In the composition, the polymerizable (e.g., photopolymerizable) monomer including the carbon-carbon double bond may include a (e.g., photopolymerizable) acryl-based monomer. The polymerizable monomer may be a precursor for an insulating polymer. The acryl-based monomer may include alkyl(meth)acrylate, ethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, 1,4-butanediol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, neopentyl glycol di(meth)acrylate, pentaerythritol di(meth)acrylate, pentaerythritol tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, dipentaerythritol di(meth)acrylate, dipentaerythritol tri(meth)acrylate, dipentaerythritol penta(meth)acrylate, pentaerythritol hexa(meth)acrylate, bisphenol A di(meth)acrylate, bisphenol A epoxy(meth)acrylate, trimethylolpropane tri(meth)acrylate, ethylene glycolmonomethylether (meth)acrylate, novolac epoxy (meth)acrylate, dipropylene glycol di(meth)acrylate, tripropylene glycol di(meth)acrylate, propylene glycol di(meth)acrylate, tris(meth)acryloyloxyethyl phosphate, or a combination thereof.

An amount of the polymerizable monomer may be greater than or equal to about 0.5 wt%, for example, greater than or equal to about 1 wt% or greater than or equal to about 2 wt%, based on a total weight of the composition. The amount of the photopolymerizable monomer may be less than or equal to about 30 wt%, for example, less than or equal to about 28 wt%, less than or equal to about 25 wt%, less than or equal to about 23 wt%, less than or equal to about 20 wt%, less than or equal to about 18 wt%, less than or equal to about 17 wt%, less than or equal to about 16 wt%, or less than or equal to about 15 wt%, based on a total weight of the composition.

The initiator in the composition may be used for polymerization of the monomers. The initiator is a compound accelerating a radical reaction (e.g., radical polymerization of monomer) by producing radical chemical species under a mild condition (e.g., by heat or light). The initiator may be a thermal initiator or a photoinitiator. The initiator is a compound capable of initiating a radical polymerization of the polymerizable acrylic monomer, a thiol compound (which will be described below), or a combination thereof by light. The initiator is not particularly limited. The initiator may be a thermal initiator. The thermal initiator may include azobisisobutyronitrile, benzoyl peroxide, and the like, but is not limited thereto. The initiator may be a photoinitiator. The photoinitiator may include a triazine-based compound, an acetophenone compound, a benzophenone compound, a thioxanthone compound, a benzoin compound, an oxime ester compound, an aminoketone compound, a phosphine or phosphine oxide compound, a carbazole-based compound, a diketone compound, a sulfonium borate-based compound, a diazo-based compound, a biimidazole-based compound, or a combination thereof, but is not limited thereto.

In the composition, an amount of the initiator may be appropriately adjusted taking into consideration the polymerizable monomers and amounts of the polymerizable monomers. In an embodiment, the initiator may be used in an amount range of about 0.01 wt% to about 10 wt%, based on a total weight of the composition, but is not limited thereto.

The composition or the composite may further include a (multi- or monofunctional) thiol compound including at least one (e.g., at least two, three, or four) thiol group(s) (for example, at a terminal end of the (multi- or monofunctional) thiol compound), a metal oxide particulate, or a combination thereof.

The metal oxide particulate may include TiO₂, SiO₂, BaTiO₃, Ba₂TiO₄, ZnO, or a combination thereof. In the composition, an amount of the metal oxide particulate may be greater than or equal to about 1 wt% and less than or equal to about 15 wt%, less than or equal to about 10 wt%, or less than or equal to about 5 wt%, based on a total weight of solids in the composition. The metal oxide particulate may have an appropriately selected diameter without a particular limit. The diameter of the metal oxide particulate may be greater than or equal to about 100 nm, for example, greater than or equal to about 150 nm, or greater than or equal to about 200 nm and less than or equal to about 1,000 nm or less than or equal to about 800 nm.

The multi-functional thiol compound may include a compound represented by Chemical Formula 1:

-   wherein, in Chemical Formula 1, R¹ is hydrogen; a substituted or     unsubstituted C1 to C30 linear or branched alkyl group; a     substituted or unsubstituted C6 to C30 aryl group; a substituted or     unsubstituted C3 to C30 heteroaryl group; a substituted or     unsubstituted C3 to C30 cycloalkyl group; a substituted or     unsubstituted C3 to C30 heterocycloalkyl group; a C1 to C10 alkoxy     group; a hydroxy group; —NH₂; a substituted or unsubstituted C1 to     C30 amine group (-NRR′, wherein R and R′ are independently hydrogen     or a C1 to C30 linear or branched alkyl group provided that both are     not simultaneously hydrogen); an isocyanate group; a halogen; -ROR′     (wherein R is a substituted or unsubstituted C1 to C20 alkylene     group and R′ is hydrogen or a C1 to C20 linear or branched alkyl     group); an acyl halide (—RC(═O)X, wherein R is a substituted or     unsubstituted C1 to C20 alkylene group and X is a halogen);     —C(═O)OR′ (wherein R′ is hydrogen or a C1 to C20 linear or branched     alkyl group); —CN; —C(═O)NRR′ (wherein R and R′ are independently     hydrogen or a C1 to C20 linear or branched alkyl group); or     —C(═O)ONRR′ (wherein R and R′ are independently hydrogen or a C1 to     C20 linear or branched alkyl group), -   L₁ is a carbon atom, a substituted or unsubstituted C1 to C30     alkylene group, a substituted or unsubstituted C3 to C30     cycloalkylene group, a substituted or unsubstituted C6 to C30     arylene group, a substituted or unsubstituted C3 to C30     heterocycloalkylene group, or a substituted or unsubstituted C3 to     C30 heteroarylene group, wherein a methylene moiety (—CH₂—) of the     substituted or unsubstituted C1 to C30 alkylene group may be     replaced by a sulfonyl moiety (—SO₂—), a carbonyl moiety (CO), an     ether moiety (—O—), a sulfide moiety (—S—), a sulfoxide moiety     (—SO—), an ester moiety (—C(═O)O—), an amide moiety (—C(═O)NR—)     (wherein R is hydrogen or a C1 to C10 alkyl group) or a combination     thereof, -   Y₁ is a single bond; a substituted or unsubstituted C1 to C30     alkylene group; a substituted or unsubstituted C2 to C30 alkenylene     group; a C1 to C30 alkylene group or a C2 to C30 alkenylene group     wherein a methylene moiety (—CH₂—) is replaced by a sulfonyl moiety     (—S(═O)₂—), a carbonyl moiety (—C(═O)—), an ether moiety (—O—), a     sulfide moiety (—S—), a sulfoxide moiety (—S(═O)—), an ester moiety     (—C (═O)O—), an amide moiety (—C(═O)NR—) (wherein R is hydrogen or a     C1 to C10 linear or branched alkyl group), an imine moiety (—NR—)     (wherein R is hydrogen or a C1 to C10 linear or branched alkyl     group), or a combination thereof, -   m is an integer of 1 or greater, -   k1 is an integer of 0 or 1 or greater, k2 is an integer of 1 or     greater, -   a sum of m and k2 is an integer of 3 or greater, and -   when Y₁ is not a single bond, m does not exceed a valence of Y₁, and     a sum of k1 and k2 does not exceed a valence of L₁.

The multi-functional thiol compound may be a dithiol compound, a trithiol compound, tetrathiol compound, or a combination thereof. For example, the thiol compound may be glycol (e.g., ethylene glycol) di-3-mercaptopropionate, glycol (e.g., ethylene glycol) dimercapto acetate, trimethylolpropane tris(3-mercaptopropionate), pentaerythritol tetrakis (3-mercaptopropionate), pentaerythritol tetrakis (2-mercaptoacetate), 1,6-hexanedithiol, 1,3-propanedithiol, 1,2-ethanedithiol, polyethylene glycol dithiol including 1 to 10 ethylene glycol repeating units, or a combination thereof.

An amount of the thiol compound may be less than or equal to about 50 wt%, less than or equal to about 45 wt%, less than or equal to about 40 wt%, less than or equal to about 35 wt%, less than or equal to about 30 wt%, less than or equal to about 25 wt%, less than or equal to about 20 wt%, less than or equal to about 15 wt%, less than or equal to about 10 wt%, less than or equal to about 9 wt%, less than or equal to about 8 wt%, less than or equal to about 7 wt%, less than or equal to about 6 wt%, or less than or equal to about 5 wt%, based on a total weight (or total solid content) of the composition. The amount of the thiol compound may be greater than or equal to about 0.1 wt%, for example, greater than or equal to about 0.5 wt%, greater than or equal to about 1 wt%, greater than or equal to about 5 wt%, greater than or equal to about 10 wt%, greater than or equal to about 15 wt%, greater than or equal to about 20 wt%, or greater than or equal to about 25 wt%, based on a total weight (or total solid content) of the composition or the composite.

The composition may further include an organic solvent (or a liquid vehicle). The organic solvent is not particularly limited. The organic solvent and an amount of the organic solvent may be appropriately determined by taking into consideration the above main components (i.e., the quantum dot, the dispersing agent, the polymerizable monomer, the initiator, and if used, the thiol compound,) and an additive and an amount of the additive which is described below. The composition may include an organic solvent in a residual amount except for a desired content of the (non-volatile) solid. Examples of the organic solvent (or liquid vehicle) may include ethyl 3-ethoxy propionate, ethylene glycols such as ethylene glycol, diethylene glycol, or polyethylene glycol; glycolethers such as ethylene glycolmonomethylether, ethylene glycolmonoethylether, diethylene glycolmonomethylether, ethylene glycoldiethylether, or diethylene glycoldimethylether; glycolether acetates such as ethylene glycol monomethyl ether acetate, ethylene glycolmonoethylether acetate, diethylene glycolmonoethylether acetate, or diethylene glycolmonobutylether acetate; propylene glycol; propylene glycolethers such as propylene glycolmonomethylether, propylene glycolmonoethylether, propylene glycolmonopropylether, propylene glycolmonobutylether, propylene glycoldimethylether, dipropylene glycoldimethylether, propylene glycoldiethylether, or dipropylene glycoldiethylether; propylene glycolether acetates such as propylene glycolmonomethylether acetate, or dipropylene glycolmonoethylether acetate; amides such as N-methylpyrrolidone, dimethyl formamide, or dimethyl acetamide; ketones such as methylethylketone (MEK), methylisobutylketone (MIBK), or cyclohexanone; petroleums such as toluene, xylene, or solvent naphtha; esters such as ethyl acetate, butyl acetate, or ethyl lactate; ethers such as diethyl ether, dipropyl ether, or dibutyl ether; aliphatic, alicyclic, or aromatic hydrocarbons; or a combination thereof.

If desired, the composition may further include various additives such as a light diffusing agent, a leveling agent, or a coupling agent in addition to the aforementioned components. The amount of the additive is not particularly limited, and may be controlled within an appropriate range wherein the additive does not cause an adverse effect on preparation of the composition and production of the quantum dot-polymer composite and optionally a patterning of the composite.

If used, the additives may be used in an amount of greater than or equal to about 0.1 wt%, for example, greater than or equal to about 0.5 wt%, greater than or equal to about 1 wt%, greater than or equal to about 2 wt%, or greater than or equal to about 5 wt%, based on a total weight of the composition, but is not limited thereto. If used, the content of the additives may be less than or equal to about 20 wt%, for example, less than or equal to about 19 wt%, less than or equal to about 18 wt%, less than or equal to about 17 wt%, less than or equal to about 16 wt%, or less than or equal to about 15 wt%, based on a total weight of the composition, but is not limited thereto.

The film of the quantum dot-polymer composite or the quantum dot-polymer composite pattern that will be described below may have for example a thickness, less than or equal to about 30 micrometers (µm), for example less than or equal to about 25 µm, less than or equal to about 20 µm, less than or equal to about 15 µm, less than or equal to about 10 µm, less than or equal to about 8 µm, less than or equal to about 7 µm and greater than or equal to about 2 µm, for example, greater than or equal to about 3 µm, greater than or equal to about 3.5 µm, or greater than or equal to about 4 µm.

In an embodiment, a patterned film includes a repeating section including a first section configured to emit a first light, wherein the first section includes the quantum dot-polymer composite. The repeating section may include a second section emitting a second light having a different maximum (photoluminescence) peak wavelength from the first light, wherein the second section may include a quantum dot-polymer composite. The quantum dot-polymer composite of the second section may include a second quantum dot configured to emit the second light. The second quantum dot may include the aforementioned quantum dot. The first light or the second light may be red light having a maximum photoluminescence peak wavelength which is present between about 600 nm and about 650 nm (e.g., about 620 nm to about 650 nm) or green light having a maximum photoluminescence peak wavelength which is present between about 500 nm and about 550 nm (e.g., about 510 nm to about 540 nm). The patterned film may further include a third section emitting or passing a third light (e.g., blue light) different from the first light and the second light. The third light may have a maximum peak wavelength ranging from about 380 nm to about 480 nm.

An embodiment provides an electronic device including the quantum dot(s). The electronic device may include a light emitting diode (LED), an organic light emitting diode (OLED), a sensor, a solar cell, an imaging sensor, or a liquid crystal display (LCD), but is not limited thereto

In an embodiment, the electronic device may be a photoluminescent device (e.g., a lighting system such as a quantum dot sheet, a quantum dot rail, or the like, or a liquid crystal display) or an electroluminescent device (e.g., quantum dot (QD) LED). In a non-limiting example, the electronic device may include a quantum dot sheet and the foregoing quantum dots may be included in the QD sheet for example, as a semiconductor nanocrystal- polymer composite.

In an embodiment, a display device includes a light source and a light emitting element (e.g., photoluminescence element), and the light emitting element includes the aforementioned quantum dot polymer composite and the light source may be configured to provide the light emitting element with incident light. The incident light may have a (photoluminescence) peak wavelength of greater than or equal to about 440 nm, for example, greater than or equal to about 450 nm and less than or equal to about 500 nm, for example, less than or equal to about 480 nm, less than or equal to about 470 nm, or less than or equal to about 460 nm.

In an embodiment, the light emitting element may include a sheet of the quantum dot polymer composite. The display device may further include a liquid crystal panel and the sheet of the quantum dot polymer composite may be disposed between the light source and the liquid crystal panel. FIG. 2 shows an exploded view of a display device. Referring to FIG. 2 , the display device may have a structure wherein a reflector, a light guide panel (LGP) and a blue LED light source (Blue-LED), the quantum dot-polymer composite sheet (QD sheet), and various optical films such as a prism, double brightness enhance film (DBEF), and the like are stacked, and a liquid crystal (LC) panel is disposed thereon.

In an embodiment, the display device may include a stacked structure including a (e.g., transparent) substrate and a light emitting layer (e.g., a photoluminescent layer) disposed on the substrate as a light emitting element. In the stacked structure, the light emitting layer includes a pattern of the quantum dot polymer composite, and the pattern may include a, e.g., at least one, repeating section configured to emit light of a predetermined wavelength. The pattern of the quantum dot polymer composite may include a first repeating section that may emit a first light, a second repeating section that may emit a second light, or a combination thereof.

The first light and the second light have a different maximum photoluminescence peak wavelength in a photoluminescence spectrum. In an embodiment, the first light may be red light (R) having a maximum photoluminescence peak wavelength of about 600 nm to about 650 nm (e.g., about 620 nm to about 650 nm), the second light may be green light (G) having a maximum photoluminescence peak wavelength of about 500 nm to about 550 nm (e.g., about 510 nm to about 550 nm), or vice versa (i.e., the first light may be a green light and the second light may be a red light).

The substrate may be a substrate including an insulation material. The substrate may include glass; various polymers such as a polyester (e.g., poly(ethylene terephthalate) (PET), poly(ethylene naphthalate) (PEN), or the like), a polycarbonate, a poly(C1 to C10 alkyl (meth)acrylate), a polyimide, a polyamide, or a combination thereof (e.g., a copolymer or a mixture thereof); a polysiloxane (e.g., PDMS); an inorganic material such as Al₂O₃ or ZnO; or a combination thereof, but is not limited thereto. A thickness of the substrate may be desirably selected taking into consideration a substrate material but is not particularly limited. The substrate may have flexibility. The substrate may have a transmittance of greater than or equal to about 50%, greater than or equal to about 60%, greater than or equal to about 70%, greater than or equal to about 80%, or greater than or equal to about 90% for light emitted from the quantum dot.

At least a portion of the substrate may be configured to cut (absorb or reflect) blue light. A layer capable of blocking (e.g., absorbing or reflecting) blue light, also referred to herein as a “blue cut layer” or “blue light absorption layer”, may be disposed on a, e.g., at least one, surface of the substrate. For example, the blue cut layer (blue light absorption layer) may include an organic material and a predetermined dye, such as, for example, a yellow dye or a dye capable of absorbing blue light and transmitting green light, red light, or green light and red light.

In an embodiment, a method of producing the stacked structure includes

-   forming a film of the above composition on a substrate; -   exposing a selected region of the film to light (e.g., having a     wavelength of less than or equal to about 400 nm); and -   developing the exposed film with an alkali developing solution to     obtain a pattern of the quantum dot polymer composite.

The details of the substrate and the composition are the same as described above.

The composition is coated to have a predetermined thickness on a substrate in an appropriate method of spin coating, slit coating, and the like. If desired, the formed film may be pre-baked (PRB). Conditions (such as a temperature, a duration, and an atmosphere) for the pre-baking may be selected appropriately.

The formed (and optionally, pre-baked) film is exposed to light of a predetermined wavelength (UV light) under a mask having a predetermined pattern. The wavelength and the intensity of light may be selected taking into consideration on the types and the amounts of the photoinitiator, the types and the amounts of quantum dots, or the like.

The film having the exposed selected area is treated (e.g., sprayed or immersed) with an alkali developing solution, and thereby the unexposed region in the film is dissolved to provide a desired pattern, which may be referred to as development. The obtained pattern may be post-baked (POB), if desired, for example, at a temperature of about 150° C. to about 230° C. for a predetermined time, for example, greater than or equal to about 10 minutes (min) or greater than or equal to about 20 min, in order to improve crack resistance and solvent resistance of the pattern.

When the quantum dot-polymer composite pattern has a plurality of repeating sections, a quantum dot-polymer composite having a desired pattern may be obtained by preparing a plurality of compositions including a quantum dot (e.g., a red light emitting quantum dot, a green light emitting quantum dot, or optionally, a blue light emitting quantum dot) having desired photoluminescence properties (a photoluminescence peak wavelength and the like) to form each repeating section and repeating the pattern formation process for each of the composition as many times (e.g., twice or more or three times or more) as desired to form a desired pattern of the quantum dot polymer composite.

In an embodiment, an ink composition of an embodiment including the population of the cadmium free quantum dots and the liquid vehicle may be used to form a pattern. For example, a pattern may be formed by depositing the ink composition including a plurality of cadmium free quantum dots, a liquid vehicle, and a monomer on a desired region of a substrate, optionally removing the liquid vehicle, and conducting a polymerization.

For example, the quantum dot-polymer composite may be in the form of a pattern of at least two different repeating color sections (e.g., RGB sections). Such a quantum dot-polymer composite pattern may be used as a photoluminescence-type color filter in a display device.

In an embodiment, a display device includes a light source and a light emitting element including a stacked structure (hereinafter, also referred to as a layered structure).

The light source may be configured to provide incident light to the light emitting element including the layered structure. The incident light may have a wavelength of about 440 nm to about 480 nm such as about 440 nm to about 470 nm. The incident light may be a third light.

In a display device including the stacked structure, the light source may include a plurality of light emitting units respectively corresponding to the first section and the second section, and the light emitting units may include a first electrode and a second electrode facing each other and an electroluminescent layer disposed between the first electrode and the second electrode. The electroluminescent layer may include an organic light emitting material.

For example, each light emitting unit of the light source may include an electroluminescent device (e.g., an organic light emitting diode (OLED)) structured to emit light of a predetermined wavelength (e.g., blue light, green light, or a combination thereof). Structures and materials of the electroluminescent device such as the organic light emitting diode (OLED) are not particularly limited.

FIG. 3A is a schematic cross-sectional view of a display device according to an embodiment and FIG. 3B is a schematic cross-sectional view of a display device according to an embodiment. Referring to FIGS. 3A and 3B, a light source includes an organic light emitting diode (OLED) emitting blue light. The organic light emitting diode OLED may include (at least two, for example, three or more) pixel electrodes 90 a, 90 b, 90 c formed on a substrate 100, a pixel defining layer 150 a, 150 b formed between the adjacent pixel electrodes 90 a, 90 b, 90 c, an organic light emitting layer 140 a, 140 b, 140 c formed on the pixel electrodes 90 a, 90 b, 90 c, and a common electrode layer 130 formed on the organic light emitting layer 140 a, 140 b, 140 c.

A thin film transistor and a substrate may be disposed under the organic light emitting diode (OLED). The pixel areas of the OLED may be disposed corresponding to the first, second, and third sections that will be described in detail below, respectively.

The stacked structure that includes a quantum dot-polymer composite pattern (e.g., including a first repeating section including green light emitting quantum dots, a second repeating section including red light emitting quantum dots, or a combination thereof) and a substrate, or the quantum dot-polymer composite pattern, may be disposed on or over a light source, for example, directly on the light source.

The sections are configured so that blue light emitted from the light source is entered thereinto and red light and green light may be emitted therefrom, respectively. Blue light emitted from the light source may pass through the third section.

The light (e.g., blue light) emitted from the light source may enter the second section 21 and the first section 11 of the pattern 170 to emit (e.g., converted) red light R and green light G, respectively. The blue light B emitted from the light source passes through or transmits from the third section 31. Over the second section 21 emitting red light, the first section 11 emitting green light, or a combination thereof, an optical element 160 may be disposed. The optical element may be a blue cut layer which cuts (e.g., reflects or absorbs) blue light and optionally green light, or a first optical filter. The blue cut layer 160 may be disposed on the upper substrate 240. The blue cut layer 160 may be disposed under the upper substrate 240 (e.g., on a bottom surface of the upper substrate 240). The blue cut layer 160 may be disposed between the upper substrate 240 and the quantum dot-polymer composite pattern and over the first section 11 and the second section 21. Details of the blue cut layer are the same as set forth for the first optical filter 310 below.

The display device may be obtained by separately fabricating the stack structure and (e.g., blue light emitting) LED or OLED and then assembling the same. Alternatively, the display device may be obtained by forming a quantum dot-polymer composite pattern directly on the LED or OLED.

In an embodiment, the display device may further include a lower substrate 210, an optical element (e.g., polarizer) 300 disposed below the lower substrate 210, and a liquid crystal layer 220 interposed between the layered structure and the lower substrate 210. The layered structure may be disposed in such a manner that a light emitting layer (i.e., the quantum dot-polymer composite pattern) faces the liquid crystal layer. The display device may further include an optical element (e.g., polarizer) 300 between the liquid crystal layer 220 and the light emitting layer. The light source may further include an LED and optionally a light guide panel.

Referring to FIG. 4 , in an embodiment, the display device includes a liquid crystal panel 200, a lower optical element 300 (e.g., polarizer) disposed on the liquid crystal panel 200, under the liquid crystal panel 200, or a combination thereof, and a backlight unit including a blue light emitting light source 110 under a lower optical element 300. The backlight unit may include a light source 110 and a light guide panel 120 (edge type). Alternatively, the backlight unit may be a direct light source without a light guide panel. The liquid crystal panel 200 may include a lower substrate 210, an upper substrate 240, and a liquid crystal layer 220 between the upper and lower substrates, and a light emitting layer (color filter layer) 230 disposed on or under the upper substrate 240. The light emitting layer 230 may include the quantum dot-polymer composite (or a pattern thereof).

A wire plate 211 is provided on an internal surface, for example, on the upper surface of the lower substrate 210. The wire plate 211 may include a plurality of gate wires and data wires that define a pixel area, a thin film transistor disposed adjacent to a crossing region of gate wires and data wires, and a pixel electrode for each pixel area, but is not limited thereto. Details of such a wire plate are not particularly limited.

The liquid crystal layer 220 may be disposed on the wire plate 211. The liquid crystal layer 220 may include an alignment layer 221 on an upper surface of the liquid crystal layer 220 and on a lower surface of the liquid crystal layer 220, to initially align the liquid crystal material included therein. Details regarding a liquid crystal material, an alignment layer material, a method of forming an alignment layer, a method of forming a liquid crystal layer, a thickness of liquid crystal layer, or the like are not particularly limited.

In an embodiment, an upper optical element or an upper polarizer 300 may be provided between the liquid crystal layer 220 and the upper substrate 240. The upper optical element or upper polarizer 300 may be disposed between the liquid crystal layer 220 (or a common electrode 231) and the light emitting layer (or the quantum dot-polymer composite pattern). A black matrix 241 may be provided under the upper substrate 240 (e.g., on a lower surface thereof). Openings within the black matrix 241 are aligned with (or provided to hide) a gate line, a data line, and a thin film transistor of a wire plate 211 on the lower substrate 210. A second section (R) including a color filter emitting red light, a first section (G) including a color filter emitting green light, a third section (B) including a color filter for emitting or transmitting blue light, or a combination thereof may be disposed in the openings within the black matrix 241 (BM). For example, the black matrix 241 may have a lattice shape. If desired, the light emitting layer may further include a, e.g., at least one, fourth repeating section. The fourth repeating section may be configured to emit light having a color (e.g., cyan, magenta, yellow, or the like) different from the colors of the light emitted from the first to third sections.

The light emitting layer (color filter layer) 230 may be on a transparent common electrode 231.

If desired, the display device may further include a blue cut filter 310, hereinafter, also referred to as a first optical filter layer 310. The first optical filter layer 310 may be disposed between upper surfaces of the second section (R) and the first section (G) and the lower surface of the upper substrate 240, or on an upper surface of the upper substrate (240). The first optical filter layer 310 may include a sheet having openings that correspond to the third section (B) (e.g., a pixel area showing, e.g., emitting, a blue color) and may be formed on portions corresponding to the first and second sections (G, R). The first optical filter layer 310 may be formed as a single body structure over the portions of the light emitting layer 230 corresponding to the first and second sections (G, R), and which are other than the portions overlapping the third section, but is not limited thereto. Alternatively, at least two first optical filter layers may be spaced apart from each other and may be disposed over each of the portions overlapping the first and the second sections, respectively.

For example, the first optical filter layer may block light having a predetermined wavelength range in the visible light range and may transmit light having another wavelength range. For example, the first optical filter layer may block blue light and transmit light other than blue light. For example, the first optical filter layer may transmit green light, red light, or yellow light (e.g., a mixture of green light and red light).

The first optical filter layer may include a polymer thin film including a dye that absorbs light having a specific wavelength, i.e., the wavelength to be blocked, a pigment that absorbs light having a specific wavelength, or a combination thereof. The first optical filter layer may block at least 80%, or at least 90%, or at least 95% of blue light having a wavelength of less than or equal to about 480 nm. With respect to the visible light having other wavelengths, the first optical filter layer may have a light transmittance of greater than or equal to about 70%, for example, greater than or equal to about 80%, greater than or equal to about 90%, or up to 100%.

The first optical filter layer may absorb and substantially block blue light having a wavelength of less than or equal to about 500 nm, and for example, may selectively transmit green light or red light. In this case, at least two first optical filter layers may be spaced apart and disposed on each of the portions overlapping the first and second sections, respectively. For example, the first optical filter layer selectively transmitting red light may be disposed on the portion overlapping the section emitting red light and the first optical filter layer selectively transmitting green light may be disposed on the portion overlapping the section emitting green light.

In an embodiment, the first optical filter layer may include a first region, a second region, or a first region and a second region. The first region of the first optical filter layer blocks (e.g., absorbs) blue light and red light and transmits light having a wavelength of a predetermined range, e.g., a wavelength greater than or equal to about 500 nm, greater than or equal to about 510 nm, or greater than or equal to about 515 nm, and less than or equal to about 550 nm, less than or equal to about 540 nm, less than or equal to about 535 nm, less than or equal to about 530 nm, less than or equal to about 525 nm, or less than or equal to about 520 nm. The second region of the first optical filter layer blocks (e.g., absorb) blue light and green light and transmits light having a wavelength of a predetermined range, e.g., a wavelength of greater than or equal to about 600 nm, greater than or equal to about 610 nm, or greater than or equal to about 615 nm and less than or equal to about 650 nm, less than or equal to about 640 nm, less than or equal to about 635 nm, less than or equal to about 630 nm, less than or equal to about 625 nm, or less than or equal to about 620 nm. The first region of the first optical filter layer may be disposed (directly) on or over a location overlapping a green light emitting section and the second region of the first optical filter layer may be disposed (directly) on or over a location overlapping a red light emitting section. The first region and the second region may be optically isolated from one another, for example, by a black matrix. The first optical filter layer may contribute to improving the color purity of a display device.

The first optical filter layer may be a reflection type filter including a plurality of layers (e.g., inorganic material layers) each having a different refractive index. For example, in the first optical layer, two layers having different refractive indices may be alternately stacked on each other. For example, a layer having a high refractive index and a layer having a low refractive index may be alternately laminated with each other.

The display device may further include a second optical filter layer 311 (e.g., red/green light or yellow light recycling layer) that is disposed between the light emitting layer 230 and the liquid crystal layer 220, and specifically between the light emitting layer 230- (e.g., the quantum dot polymer composite layer) and the upper polarizer 300. The second optical filter layer 311 may transmit at least a portion of a third light, and reflect at least a portion of a first light, a second light, or a first light and a second light. The second optical filter layer may reflect light having a wavelength of greater than 500 nm. The first light may be green (or red) light, the second light may be red (or green) light, and the third light may be blue light.

The quantum dots may be used in a luminescent layer in a quantum dot based electroluminescent device (see FIG. 5 ). The electroluminescent device may include an anode 1 and a cathode 5 facing each other; a quantum dot emission layer 3 disposed between the anode 1 and the cathode 5 and including a plurality of quantum dots, and a hole auxiliary layer 2 disposed between the anode and the quantum dot emission layer. The hole auxiliary layer may include a hole injecting layer (HIL), a hole transporting layer (HTL), an electron blocking layer (EBL), or a combination thereof. The hole auxiliary layer may include a suitable organic/inorganic material having a hole property. The electroluminescent device may further include an electron auxiliary layer 4 between the cathode and the quantum dot emission layer. The electron auxiliary layer may include an electron injecting layer (EIL), an electron transporting layer (ETL), a hole blocking layer (HBL), or a combination thereof. The electron auxiliary layer may include a suitable organic/inorganic material having an electron property.

Hereinafter, embodiments are illustrated in more detail with reference to specific examples. However, they are exemplary examples of the present disclosure, and the present disclosure is not limited thereto.

EXAMPLES Analysis Method 1. Photoluminescence Analysis

A photoluminescence (PL) spectrum of the produced nanocrystals are obtained using a Hitachi F-7000 spectrometer at an irradiation wavelength of 372 nanometers (nm).

2. Ultraviolet (UV) Spectroscopy Analysis

UV spectroscopy analysis is performed using an Agilent Cary 5000 spectrometer to obtain a UV-Visible absorption spectrum.

3. Inductively Coupled Plasma (ICP) Analysis

An inductively coupled plasma-atomic emission spectroscopy (ICP-AES) analysis is performed using Shimadzu ICPS-8100.

Synthesis is performed under an inert gas atmosphere (nitrogen flowing condition) unless particularly mentioned.

Synthesis of Quantum Dot Having a ZnTeSe Core and a ZnSe/ZnS Shell Example 1

Selenium and tellurium are dispersed in trioctylphosphine (TOP) to obtain a 0.4 molar (M) Se/TOP stock solution and a 0.5 M Te/TOP stock solution. The Se/TOP stock solution, the Te/TOP stock solution, and an organic ligand including oleyl amine, and lithium aluminum hydride are mixed at room temperature to provide a reaction solution.

In a 300 milliliter (mL) reaction flask, 0.9 millimoles (mmol) of zinc acetate is dissolved in octadecene together with oleic acid, and is treated under vacuum at 120° C. In one hour, an atmosphere in the reaction flask is converted into nitrogen and then a reaction system is heated to 200° C.

The reaction solution is injected into the heated reaction system and the reaction is conducted.

After the reaction is terminated, the reaction flask is cooled to room temperature and acetone is added thereto to obtain precipitates, which are separated via centrifugation. The obtained ZnTeSe quantum dots are dispersed in toluene.

The used amounts of Zn, Se, and Al with respect to one mole of Te is 9 moles, 0.5 moles, and 1 mole, respectively.

With respect to the quantum dots as prepared, an inductively coupled plasma atomic emission spectroscopic analysis is made and the results are summarized in Table 1.

With respect to the quantum dots as prepared, an ultraviolet-visible (UV-Vis) absorption spectroscopy analysis and a photoluminescent spectroscopy analysis are made and the results are summarized in FIG. 6 and Table 2.

Example 2

A ZnTeSe quantum dot is prepared in the same manner as Example 1 except for using Alane N,N-dimethylamine complex instead of lithium aluminum hydride.

With respect to the quantum dots as prepared, an inductively coupled plasma atomic emission spectroscopic analysis is made and the results are summarized in Table 1.

With respect to the quantum dots as prepared, a UV-Vis absorption spectroscopy analysis and a photoluminescent spectroscopy analysis are made and the results are summarized in Table 2.

Example 3

A ZnTeSe quantum dot is prepared in the same manner as Example 1 except for using diisobutylaluminum hydride instead of lithium aluminum hydride.

With respect to the quantum dots as prepared, an inductively coupled plasma atomic emission spectroscopic analysis is made and the results are summarized in Table 1.

With respect to the quantum dots as prepared, a UV-Vis absorption spectroscopy analysis and a photoluminescent spectroscopy analysis are made and the results are summarized in Table 2.

Comparative Example 1

A ZnTeSe quantum dot is prepared in the same manner as Example 1 except for using lithium triethylborohydride instead of lithium aluminum hydride.

With respect to the quantum dots as prepared, an inductively coupled plasma atomic emission spectroscopic analysis is made and the results are summarized in Table 1.

With respect to the quantum dots as prepared, a UV-Vis absorption spectroscopy analysis and a photoluminescent spectroscopy analysis are made and the results are summarized in FIG. 7 and Table 2.

Comparative Example 2

A semiconductor nanocrystal particle is prepared in the same manner as Example 1 except for not using the lithium aluminum hydride.

With respect to the particles as prepared, a UV-Vis absorption spectroscopy analysis and a photoluminescent spectroscopy analysis are made. The particles do not show, e.g., exhibit, luminous properties. The particles do not show, e.g., exhibit, a Valley Depth. With respect to the particles as prepared, an inductively coupled plasma atomic emission spectroscopic analysis is made and the results confirm that the particles do not include aluminum.

Example 4

In a 300 mL reaction flask, trioctylamine (TOA) is placed and zinc acetate and oleic acid are added thereto, then the mixture is vacuum-treated at 120° C. for 10 minutes. After the atmosphere in the flask is replaced with an inert atmosphere, the flask is heated to 200° C.

A toluene dispersion of the ZnTeSe quantum dots prepared in Example 1 is injected rapidly and then Se/TOP stock solution are added thereto and the reaction proceeds for one hour (formation of a ZnSeS layer).

After the completion of the reaction, the flask is cooled to room temperature and the prepared ZnTeSe/ZnSe core-shell quantum dots are recovered via precipitation using ethanol and centrifugation. The obtained core-shell quantum dots are dispersed in toluene.

9 moles of the zinc precursor is used for 1 mole of the Se precursor.

With respect to the quantum dots as prepared, an inductively coupled plasma atomic emission spectroscopic analysis is made and the results are summarized in Table 1.

With respect to the quantum dots as prepared, a UV-Vis absorption spectroscopy analysis and a photoluminescent spectroscopy analysis are made and the results are summarized in FIG. 8 and Table 2.

Example 5

A ZnTeSe/ZnSe/ZnS core-shell quantum dot is prepared in the same manner as Example 4 except that 0.5 M of S/TOP stock solution is prepared by dissolving sulfur in trioctyl phosphine and the S/TOP stock solution is injected in addition to the Se/TOP stock solution. The obtained core-shell quantum dots are dispersed in toluene.

With respect to 9 moles of the zinc precursor, 1 mole of the Se precursor and 1 mole of the S precursor are used respectively.

With respect to the quantum dots as prepared, an inductively coupled plasma atomic emission spectroscopic analysis is made and the results are summarized in Table 1.

With respect to the quantum dots as prepared, a UV-Vis absorption spectroscopy analysis and a photoluminescent spectroscopy analysis are made and the results are summarized in Table 2 and FIG. 9 .

TABLE 1 Mole ratio (X:Te) ZnTe_(x)Se_(1-x) Zn Se Te Al and Li S x Example 1 2.88:1 0.49:1 1:1 Al 1.02:1 Li 0.21:1 0:1 0.67 Example 2 2.34:1 0.44:1 1:1 Al 0.54:1 0:1 0.69 Example 3 2.40:1 0.44:1 1:1 Al 0.54:1 0:1 0.70 Comparative Example 1 1.46:1 0.45:1 1:1 Li 0.5:1 0:1 0.69 Example 4 3.11:1 1.24:1 1:1 Al 0.37:1 0:1 0.45 Example 5 4.59:1 0.51:1 1:1 Al 0.24:1 2.11:1 0.66

TABLE 2 UV 1^(st) peak (nm) Valley Depth (VD) PL Peak (nm) Quantum Yield (QY) (%) FWHM (nm) Example 1 456 0.19 476 4.3 24.5 Example 2 451 0.03 487 0.8 24.0 Example 3 466 0.04 493 0.8 20.3 Comparative Example 1 470 0 480 0.1 20 Example 4 505 0.07 526 17 27 Example 5 508 0.04 524 13 28.2

The results of Table 2 confirm that the quantum dots of the Examples may have a valley depth together with enhanced optical properties.

While this disclosure has been described in connection with what is presently considered to be practical example embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims. 

What is claimed is:
 1. A core-shell quantum dot comprising a core comprising a first semiconductor nanocrystal material; and a semiconductor nanocrystal shell disposed on the core, wherein the core-shell quantum dot comprises zinc, tellurium, selenium, and aluminum, wherein an ultraviolet-visible absorption spectrum of the core-shell quantum dot has a first absorption peak and a valley adjacent to the first absorption peak, and a valley depth defined by the following equation is greater than or equal to 0.01: valley depth = (Abs_(first)-Abs_(valley))/ Abs_(first) wherein Abs_(first) is an absorption intensity at a first absorption peak wavelength and Abs_(valley) is an absorption intensity at a lowest point of the valley; and wherein the first semiconductor nanocrystal material comprises zinc, tellurium, and selenium, and the semiconductor nanocrystal shell comprises zinc and at least one of selenium and sulfur.
 2. The core-shell quantum dot of claim 1, wherein the valley depth is from about 0.02 to about 0.19.
 3. The core-shell quantum dot of claim 1, wherein the core-shell quantum dot has a quantum efficiency of greater than or equal to about 20%, and optionally wherein the valley depth is greater than or equal to about 0.03.
 4. The core-shell quantum dot of claim 1, wherein in the core-shell quantum dot, a mole ratio of tellurium with respect to selenium is greater than about 0.05:1 and less than or equal to about 4:1.
 5. The core-shell quantum dot of claim 1, wherein the core-shell quantum dot further comprises sulfur and a mole ratio of sulfur to zinc is greater than or equal to about 0.1:1 and less than or equal to about 0.6:1; or wherein in the core-shell quantum dot, a mole ratio of tellurium with respect to zinc is greater than or equal to about 0.02 and less than or equal to about 0.5:1.
 6. The core-shell quantum dot of claim 1, wherein the core-shell quantum dot does not comprise cadmium.
 7. The core-shell quantum dot of claim 1, wherein the core comprises ZnTe_(x)Se_(1-x), wherein x is greater than or equal to 0.5 and less than or equal to about 0.9, and the semiconductor nanocrystal shell comprises ZnSe, ZnS, ZnSeS, or a combination thereof.
 8. The core-shell quantum dot of claim 1, wherein the core-shell quantum dot has a maximum photoluminescent peak in a wavelength range of greater than or equal to about 490 nanometers and less than or equal to about 550 nanometers, and optionally wherein a full width at half maximum of the maximum photoluminescent peak is less than or equal to about 50 nanometers.
 9. The core-shell quantum dot of claim 1, wherein in the core-shell quantum dot, a mole ratio of aluminum to tellurium is greater than or equal to about 0.01:1 and less than or equal to about 1:1.
 10. A display device comprising a light source and a light emitting element, wherein the light emitting element comprises a quantum dot-polymer composite, wherein the quantum dot-polymer composite comprises a polymer matrix; and a plurality of quantum dots dispersed in the polymer matrix, wherein the plurality of quantum dots comprises the core-shell quantum dot of claim 1; and the light source is configured to provide the light emitting element with incident light.
 11. A quantum dot comprising zinc, tellurium, selenium, and aluminum, wherein the quantum dot is configured to emit light having a maximum peak wavelength of less than or equal to about 550 nm; wherein the quantum dot does not comprise an indium phosphide; and wherein an ultraviolet-visible absorption spectrum of the quantum dot has a first absorption peak and a valley adjacent to the first absorption peak; and a valley depth defined by the following equation is greater than or equal to 0.01: valley depth =(Abs_(first)- Abs_(valley))/Abs_(first) wherein Abs_(first) is an absorption intensity at the first absorption peak and Abs_(valley) is an absorption intensity at a lowest point of the valley.
 12. The quantum dot of claim 11, wherein the quantum dot comprises ZnTe_(x)Se_(1-x), wherein x is greater than or equal to about 0.5 and less than or equal to about 0.95.
 13. The quantum dot of claim 11, wherein in the quantum dot, a mole ratio of tellurium with respect to selenium is greater than 0.05:1 and less than or equal to about 4:1.
 14. The quantum dot of claim 11, wherein the quantum dot does not comprise cadmium.
 15. The quantum dot of claim 11, wherein the quantum dot is configured to exhibit a maximum photoluminescent peak having a full width at half maximum of less than or equal to about 40 nanometers and the quantum dot has a quantum efficiency of greater than or equal to about 20%, and optionally wherein the maximum peak wavelength is greater than or equal to about 490 nanometers and less than or equal to about 530 nanometers.
 16. The quantum dot of claim 11, wherein the valley depth is greater than or equal to about 0.1.
 17. The quantum dot of claim 11, wherein the first absorption peak and the lowest point of the valley are present in a wavelength range of greater than or equal to 420 nanometers and less than or equal to about 500 nanometers.
 18. A display device comprising a light source, and a light emitting element, wherein the light emitting element comprises a quantum dot-polymer composite, wherein the quantum dot-polymer composite comprises a polymer matrix; and a plurality of quantum dots dispersed in the polymer matrix, wherein the plurality of quantum dots comprises the quantum dot of claim 11; and the light source is configured to provide the light emitting element with incident light.
 19. An electroluminescent device comprising an anode and a cathode, and a quantum dot emission layer disposed between the anode and the cathode, wherein the quantum dot emission layer comprises the quantum dot of claim
 11. 20. An electroluminescent device comprising an anode and a cathode, and a quantum dot emission layer disposed between the anode and the cathode, wherein the quantum dot emission layer comprises the core-shell quantum dot of claim
 1. 